Analysis of Damage Degradation Parameters of Concrete Subjected to Freezing-thawing Cycles and Chemical Attack(PDF)

《建筑科学与工程学报》[ISSN:1673-2049/CN:61-1442/TU]

Issue:
2011年04期
Page:
1-8
Research Field:
Publishing date:
2011-12-20

Info

Title:
Analysis of Damage Degradation Parameters of Concrete Subjected to Freezing-thawing Cycles and Chemical Attack
Author(s):
YU Hong-fa1;  SUN Wei2;  MA Hai-yan1;  ZHANG Yun-sheng2;  WANG Jia-chun1; 3;  CHEN Shu-dong1; 4
1. Department of Civil Engineering, Nanjing University of Aeronautics and Astronautics, Nanjing 210016, Jiangsu, China; 2. School of Materials Science and Engineering, Southeast University, Nanjing 210096, Jiangsu, China; 3. Department of Civil Engineer
Keywords:
concrete;  single factor;  double factor;  initial damage velocity;  second initial damage velocity;  damage acceleration;  freezing-thawing life
PACS:
TU528
DOI:
-
Abstract:
Initial damage velocity(IDV)and damage acceleration(DA)of concrete subjected to single or combined factors, such as freezing-thawing and chemical attacks, were obtained through a mass of durability experiments, and the database was also established. Regression and correlative analysis of the database were carried out by using SPSS10.0 software. Results show that IDV and DA of concrete are determined by the environment, climate and load state and at the same time are closely influenced by the raw materials, mixture ratio and curing condition. Lower water cement ratio and higher relative humidity can reduce IDA and DA of concrete subjected to either signal or double factors. For concrete subjected to single factor, IDV and DA can be decreased by adding steel fibers, while for concrete subjected to double factors, IDV and DA can be decreased by adding higher elasticity module polyethylene fibers or mineral admixture. It is evident that the larger the IDV and DA are, the shorter the freezing-thawing life is.

References:

[1] 余红发,孙 伟,张云升,等.在冻融或腐蚀环境下混凝土使用寿命预测方法Ⅰ——损伤演化方程与损伤失效模式[J].硅酸盐学报,2008,36(增1):128-135. YU Hong-fa,SUN Wei,ZHANG Yun-sheng,et al.Service Life Prediction Method of Concrete Subjected to Freezing-thawing Cycles and/or Chemical Attack Ⅰ—Damage Development Equation and Degradation Mode[J].Journal of the Chinese Ceramic Society,2008,36(S1):128-135.
[2]黄 海,罗友丰,陈志英,等.SPSS10.0 for Windows 统计分析[M].北京:人民邮电出版社,2001. HUANG Hai,LUO You-feng,CHEN Zhi-ying,et al.Statistical Analysis of SPSS10.0 for Windows [M].Beijing:The People's Posts and Telecommunications Press,2001.
[3]余红发.盐湖地区高性能混凝土的耐久性、机理与使用寿命预测方法[D].南京:东南大学,2004. YU Hong-fa.Study on High Performance Concrete in Salt Lake:Durability,Mechanism and Service Life Prediction[D].Nanjing:Southeast University,2004.
[4]王永逵,陆吉祥.材料试验和质量分析的数学方法[M].北京:中国铁道出版社,1990:162-168. WANG Yong-kui,LU Ji-xiang.Mathematical Method of Materials Test and Quality Analysis[M].Beijing:China Railway Publishing House,1990:162-168.
[5]张云清,余红发,王甲春.盐冻条件下混凝土结构表面的损伤规律研究[J].中国公路学报,2009,22(4):57-63. ZHANG Yun-qing,YU Hong-fa,WANG Jia-chun.Study of Surface Damage Rule of Concrete Structure Exposed to Salt Freezing Condition[J].China Journal of Highway and Transport,2009,22(4):57-63.
[6]张云清,余红发,孙 伟,等.硫酸镁溶液对应力作用下混凝土抗冻性的影响[J].交通运输工程学报,2010,10(6):15-19. ZHANG Yun-qing,YU Hong-fa,SUN Wei,et al.Effect of Magnesium Sulfate Solution on Frost Resistance of Concrete Under Stress Condition[J].Journal of Traffic and Transportation Engineering,2010,10(6):15-19.

Memo

Memo:
-
Last Update: 2011-12-20