Mechanical Properties of Manufactured Sand Concrete with Different Stone Powder Content After High Temperatures(PDF)

《建筑科学与工程学报》[ISSN:1673-2049/CN:61-1442/TU]

Issue:
2021年03期
Page:
80-89
Research Field:
Publishing date:

Info

Title:
Mechanical Properties of Manufactured Sand Concrete with Different Stone Powder Content After High Temperatures
Author(s):
XIE Kai-zhong12 LIU Zhen-wei1 ZHU Mao-jin1 MA Da-li1
(1. College of Civil Engineering and Architecture, Guangxi University, Nanning 530004, Guangxi, China; 2. Key Laboratory of Engineering Disaster Prevention and Structural Safety of Ministry of Education,Guangxi University, Nanning 530004, Guangxi, China)
Keywords:
manufactured sand concrete high temperature stone powder content strength microstructure
PACS:
TU528
DOI:
10.19815/j.jace.2020.09070
Abstract:
Based on the parameters of temperature and stone powder content, 210 cube specimens(100 mm×100 mm×100 mm)of manufactured sand concrete(MSC)were designed. The physical and mechanical properties after high temperature were tested. The mass loss rate, compressive strength and splitting tensile strength of specimens were obtained. The degradation models of compressive strength and splitting tensile strength after high temperature of MSC were established. The micro-mechanism of mechanical properties deterioration of MSC after high temperature were investigated by X-ray diffraction(XRD)and scanning electron microscope(SEM). The evaluation formulas of compressive strength and splitting tensile strength of MSC after high temperature based on the maximum fire temperature and mass loss rate were put forward. The results indicate that with the increase of temperature, the surface color of MSC specimens change from gray to reddish brown, and finally to gray. Temperature crevice and spalling arise on the surface of the specimen under high temperature. The mass loss rate of the specimen increases significantly with the increase of stone powder content. The compressive strength and splitting tensile strength of concrete decrease with temperature rise. The compressive strength and splitting tensile strength of the MSC specimens firstly increase, then decrease when the stone powder content is increased, and the concrete strength goes for a maximum when the content of stone powder reaches 10%(mass fraction). The deterioration model of compressive strength and splitting tensile strength of MSC after high temperature based on the measured results has good fitting degree. The amount of hydration products of MSC such as ettringite and calcium hydroxide can be promoted by adding stone powder. The cement hydrate dehydrates and decomposes in MSC, which makes the internal cracks and pores of concrete increase after high temperature of 700 ℃.

References:

[1] MA Q M,GUO R X,ZHAO Z M,et al.Mechanical Properties of Concrete at High Temperature — A Review[J].Construction and Building Materials,2015,93:371-383.
[2]王海龙,俞秋佳,孙晓燕,等.高温作用后混凝土损伤与耐久性能评价[J].江苏大学学报:自然科学版,2014,35(2):238-242.
WANG Hai-long,YU Qiu-jia,SUN Xiao-yan,et al.Durability and Damage Evaluation of Concrete Subjected to High Temperature[J].Journal of Jiangsu University:Natural Science Edition,2014,35(2):238-242.
[3]秦 斌.海水海砂混凝土基本力学性能研究[J].混凝土,2019(2):90-91.
QIN Bin.Basic Mechanical Properties of Seawater and Sea Sand Concrete[J].Concrete,2019(2):90-91.
[4]崔 壮,秦拥军,许富威,等.沙漠砂混凝土研究现状[J].混凝土,2020(2):106-110.
CUI Zhuang,QIN Yong-jun,XU Fu-wei,et al.Research Status of Desert Sand Concrete[J].Concrete,2020(2):106-110.
[5]李志强,王国庆,杨 森,等.沙漠砂混凝土力学性能及应力-应变本构关系试验研究[J].应用力学学报,2019,36(5):1131-1137,1261.
LI Zhi-qiang,WANG Guo-qing,YANG Sen,et al.Experimental Study on Mechanical Properties and Stress-strain Constitutive Relations of Desert Sand Concrete[J].Chinese Journal of Applied Mechanics,2019,36(5):1131-1137,1261.
[6]李 波,周海龙,吕振国,等.高强机制砂混凝土工作性及力学性能的试验研究[J].硅酸盐通报,2020,39(6):1765-1771,1797.
LI Bo,ZHOU Hai-long,LYU Zhen-guo,et al.Experimental Study on Workability and Mechanical Properties of High Strength Manufactured Sand Concrete[J].Bulletin of the Chinese Ceramic Society,2020,39(6):1765-1771,1797.
[7]ZHANG G X,SONG J X,YANG J S,et al.Performance of Mortar and Concrete Made with a Fine Aggregate of Desert Sand[J].Building and Environment,2006,41(11):1478-1481.
[8]李北星,周明凯.石灰岩机制砂中石粉作掺合料对混凝土工作性和强度的影响[J].公路,2007(12):141-145.
LI Bei-xing,ZHOU Ming-kai.Effect of Quarry Waste Powder in Limestone Manufactured Sand as Mineral Admixture on Workability and Strength of Concretes[J].Highway,2007(12):141-145.
[9]陈正发,刘桂凤,秦彦龙,等.恶劣环境下机制砂混凝土的强度和耐久性能[J].建筑材料学报,2012,15(3):391-394.
CHEN Zheng-fa,LIU Gui-feng,QIN Yan-long,et al.Strength and Durability of Concrete with Manufactured-sand in Severe Environment[J].Journal of Building Materials,2012,15(3):391-394.
[10]赵顺波,苏延峰,李长永,等.机制砂再生粗骨料混凝土配筋柱偏心受压承载力研究[J].混凝土,2013(9):26-28.
ZHAO Shun-bo,SU Yan-feng,LI Chang-yong,et al.Research on Eccentric Compressive Resistance of Reinforced MSRAC Columns[J].Concrete,2013(9):26-28.
[11]陈正发,刘桂凤,徐建民.机制砂混凝土在高温后的强度和耐久性研究[J].混凝土,2011(10):46-48.
CHEN Zheng-fa,LIU Gui-feng,XU Jian-min.Study on the Strength and Durability of Concrete with Manufactured-sand Under Condition of High Temperature[J].Concrete,2011(10):46-48.
[12]齐锦程.掺机制砂高性能混凝土高温后强度及孔隙劣化试验[J].中国科技论文,2018,13(19):2219-2222.
QI Jin-cheng.Experimental Study on the Degradation of Strength and Pore of HPC with Added Manufactured Sand[J].China Sciencepaper,2018,13(19):2219-2222.
[13]柴松华.机制砂高性能混凝土高温后的力学性能试验研究及机理分析[D].太原:太原理工大学,2014.
CHAI Song-hua.Experimental Study and Mechanism Analysis on Mechanical Property of High Performance Concrete with Manufactured Sand After High Temperature[D].Taiyuan:Taiyuan University of Technology,2014.
[14]任雪振,韩 阳,张 彦.高温后机制砂混凝土与钢筋黏结性能试验研究[J].混凝土,2020(10):51-54,58.
REN Xue-zhen,HAN Yang,ZHANG Yan.Post-high-temperature Experimental Study on the Manufactured Sand Concrete and Rebar Bonding Performance[J].Concrete,2020(10):51-54,58.
[15]陈正发,秦彦龙,刘桂凤,等.高温后机制砂混凝土的本构关系试验研究[J].混凝土,2013(12):72-74,86.
CHEN Zheng-fa,QIN Yan-long,LIU Gui-feng,et al.Experimental Study on Constitutive Relation of Concrete with Manufactured-sand After High Temperatures[J].Concrete,2013(12):72-74,86.
[16]杨卓强,刘元珍.石粉掺量对机制砂高性能混凝土强度及耐久性能影响研究[J].混凝土,2018(7):69-71,75.
YANG Zhuo-qiang,LIU Yuan-zhen.Effect of Stone Powder Content on Strength and Durability of High Performance Concrete with Machine-made Sand[J].Concrete,2018(7):69-71,75.
[17]XIE K Z,BAI M Y,QING Z G,et al.Study on Durability of Manufactured Sand Based on Stone Powder Content[J].Science of Advanced Materials,2018,10(11):1608-1614.
[18]谢开仲,王红伟,肖 杰,等.石粉含量对机制砂混凝土力学性能影响试验[J].建筑科学与工程学报,2019,36(5):31-38.
XIE Kai-zhong,WANG Hong-wei,XIAO Jie,et al.Experiment on Influence of Stone Powder Content on Mechanical Properties of Manufactured Sand Concrete[J].Journal of Architecture and Civil Engineering,2019,36(5):31-38.
[19]雷 瑜,黄昌华,杨海成,等.砂岩石粉含量对中等强度等级机制砂混凝土性能的影响研究[J].建筑结构,2017,47(增1):950-953.
LEI Yu,HUANG Chang-hua,YANG Hai-cheng,et al.Research on the Effect of Sandstone Powder Content on the Properties for Medium-strength Sandstone Concrete[J].Building Structure,2017,47(S1):950-953.
[20]王 青,江 满,徐 港,等.机制砂石粉含量对泵送混凝土强度的影响[J].混凝土,2018(2):102-106.
WANG Qing,JIANG Man,XU Gang,et al.Effect of Mechanical Gravel Powder Content on Strength of Pumped Concrete[J].Concrete,2018(2):102-106.
[21]AN J,KIM S,NAM B H.Effect of Aggregate Mineralogy and Concrete Microstructure on Thermal Expansion and Strength Properties of Concrete[J].Applied Science,2017,7(12):1307.
[22]GUPTA L K,VYAS A K.Impact on Mechanical Properties of Cement Sand Mortar Containing Waste Granite Powder[J].Construction and Building Materials,2018,191:155-164.
[23]钱在兹,吴 慧.混凝土高温后的扫描电镜实验研究[J].福州大学学报:自然科学版,1996,24(增):34-38.
QIAN Zai-zi,WU Hui.Experimental Study on SEM of Concrete After High Temperature[J].Journal of Fuzhou University:Natural Science,1996,24(S):34-38.
[24]SHEN W G,LIU Y,WANG Z W,et al.Influence of Manufactured Sand's Characteristics on Its Concrete Performance[J].Construction and Building Materials,2018,172:574-583.
[25]YANG H F,LIANG D Y,DENG Z H,et al.Effect of Limestone Powder in Manufactured Sand on the Hydration Products and Microstructure of Recycled Aggregate Concrete[J].Construction and Building Materials,2018,188:1045-1049.
[26]吴 波.火灾后钢筋混凝土结构的力学性能[M].北京:科学出版社,2003.
WU Bo.Mechanical Properties of Reinforced Concrete Structures After Fire[M].Beijing:Science Press,2003.
[27]GALETAKIS M,RAKA S.Utilization of Limestone Dust for Artificial Stone Production:An Experimental Approach[J].Minerals Engineering,2004,17(2):355-357.
[28]范 波,吴 达,马文峰,等.石灰石粉对混凝土界面过渡区黏结强度的影响[J].非金属矿,2018,41(4):46-47.
FAN Bo,WU Da,MA Wen-feng,et al.Effect of Ground Limestone on Bonding Strength of Concrete Interfacial Transition Zone[J].Non-metallic Mines,2018,41(4):46-47.
[29]吕天启,赵国藩,林志伸,等.高温后静置混凝土的微观分析[J].建筑材料学报,2003,6(2):135-141.
LÜ Tian-qi,ZHAO Guo-fan,LIN Zhi-shen,et al.Microscopic Analysis of Long Standing Concrete After High Temperature[J].Journal of Building Materials,2003,6(2):135-141.
[30]万夫雄,赵鹏辉,连会杰,等.高温后再生混凝土强度与微观机理[J].混凝土,2017(1):52-55.
WAN Fu-xiong,ZHAO Peng-hui,LIAN Hui-jie,et al.Strength of Recycled Concrete After High Temperature and Its Microstructure Mechanism[J].Concrete,2017(1):52-55.

Memo

Memo:
-
Last Update: 2021-05-20