|本期目录/Table of Contents|

[1]赵国藩,陈凤山,高潮.CFRP加固海工混凝土结构的抗Cl-侵蚀试验研究[J].建筑科学与工程学报,2008,25(03):1-5.
　ZHAO Guo-fan,CHEN Feng-shan,GAO Chao.Test Research on Chloride Ions Attack of Coastal Concrete Structure Reinforced by CFRP[J].Journal of Architecture and Civil Engineering,2008,25(03):1-5.
点击复制

CFRP加固海工混凝土结构的抗Cl-侵蚀试验研究(PDF)
分享到：

《建筑科学与工程学报》[ISSN:1673-2049/CN:61-1442/TU]

卷:
25卷
期数:
2008年03期
页码:
1-5
栏目:
出版日期:
2008-09-20

文章信息/Info

Title:
Test Research on Chloride Ions Attack of Coastal Concrete Structure Reinforced by CFRP
作者:
赵国藩1,陈凤山2,高潮2
1.大连理工大学海岸和近海工程国家重点实验室,辽宁大连116024; 2.大连水产学院土木工程学院,辽宁大连116023
Author(s):
ZHAO Guo-fan1, CHEN Feng-shan2, GAO Chao 2
1. State Key Laboratory of Coastal and Offshore Engineering, Dalian University of Technology, Dalian 116024, Liaoning, China; 2. School of Civil Engineering, Dalian Fisheries University, Dalian 116023,Liaoning, China
关键词:
碳纤维复合材料;  Cl-;  阻隔作用;  防护体系;  剩余耐久寿命
Keywords:
carbon fiber reinforced polymer;  chloride ion;  obstructing function;  system of corrosion prevention;  residual durability life
分类号:
TU528.33
DOI:
-
文献标志码:
A
摘要:
通过2组室内快速渗透试验,验证了混凝土表面黏贴碳纤维复合材料(CFRP)能够有效地阻止Cl-向混凝土中渗透:第1组试验验证了CFRP材料对Cl-阻隔的有效性; 第2组试验则进一步验证了在混凝土表面黏贴CFRP对Cl-阻隔的作用。试验结果表明,对于海工混凝土结构,表面黏贴CFRP除了具有加固的作用以外,还具有阻隔Cl-的作用,进而可以延长加固结构的腐蚀诱导期。因此,当进行沿海混凝土结构CFRP加固设计时,建议考虑将CFRP和其他表面防护措施共同使用,并组成完整的表面防护体系。考虑到表面黏贴CFRP对Cl-的隔离作用是在一定时间内有效的,基于Fick第二定律,给出了海工混凝土结构外包CFRP加固后的寿命预测方程,为沿海混凝土结构CFRP加固设计及加固后耐久性评估提供了依据。
Abstract:
The function that carbon fiber reinforced polymer(CFRP)bonded externally prevents effectively chloride ions from entering concrete was confirmed by two groups of laboratory accelerated penetration tests. The effectiveness of CFRP material to prevent chloride ions was confirmed by tests of type 1; and similar conclusion was also drawn in the test of type 2 when CFRP externally bonded on concrete specimens. Test results show that, for coastal concrete structures, there is not only function of strengthening of CFRP, but also that of preventing chloride ions from penetrating into concrete, and consequently to prolong the initiation period of rebars corrosion. It is also confirmed by test that there is similar function of CFRP and coating on the surface of concrete to shield concrete against chloride ions. Therefore, it is suggested that CFRP bonded externally and coating or other surface prevention measures are applied jointly to form an integrated surface prevention system when CFRP is applied in strengthening coastal concrete structures. Considering the limitation involving with time of the effective shielding function of CFRP, an equation used for residual lifetime prediction of concrete structures bonded externally with CFRP is derived from Fick's dispersion law. Overall, the conclusion may be used for reference when CFRP is applied to strengthen coastal concrete structures.

参考文献/References:

[1] 潘德强,洪定海,郑恩慧,等.华南海港钢筋混凝土码头锈蚀破坏调查报告[R].南京:南京水利科学院,1981:1-8. PAN De-qiang,HONG Ding-hai,ZHENG En-hui,et al.Investigation Report of Concrete Corrosion and Damage of Seaport Wharf in South China[R].Nanjing:Nanjing Hydraulic Research Institute,1981:1-8.
[2]金伟良,赵羽习.混凝土结构耐久性[M].北京:科学出版社,2002:51-54. JIN Wei-liang,ZHAO Yu-xi.Durability of Concrete Structures[M].Beijing:Science Press,2002:51-54.
[3]陈奋健.既有海工混凝土结构耐久性及维修加固对策[C]//邢 锋,明海燕.沿海地区混凝土结构耐久性及其设计方法.北京:人民交通出版社,2004:480-486. CHEN Fen-jian.Durability and Maintaining Countermeasure of Existing Marine Concrete Structure[C]//XING Feng,MING Hai-yan.Durability and Design Method of Concrete Structure in Littoral.Beijing:China Communications Press,2004:480-486.
[4]NT Build 443,Concrete,Hardened:Accelerated Chlor-ide Penetration[S].
[5]JTJ 275-2000,海港工程混凝土防腐蚀技术规范[S]. JTJ 275-2000,Criterion of Anti-corrosion Technology in Marine Engineering Concrete[S].
[6]JTJ 270-98,水运工程混凝土试验规程[S]. JTJ 270-98,Test Criterion of Water Carriage Engin-eering Concrete[S].
[7]MARUYAMA K.Strengthening of Concrete Structures Using Continuous Fiber Reinforcing Materials[C]//University of British Columbia.Proceedings of the Third International Conference on Concrete Under Sever Conditions.Vancouver:University of British Columbia Press,2001:1987-1996.

相似文献/References:

[1]马昆林,谢友均,刘运华,等.砂浆固化Cl-性能的影响因素[J].建筑科学与工程学报,2007,24(01):37.
　MA Kun-lin,XIE You-jun,LIU Yun-hua,et al.Influence Factors on Performance of Mortar Solidifying Chloride[J].Journal of Architecture and Civil Engineering,2007,24(03):37.

备注/Memo

备注/Memo:
收稿日期:2008-07-02
作者简介:赵国藩(1924-),男,山西汾阳人,教授,博士研究生导师,中国工程院院士,E-mail:fengshan.chen@163.com。
更新日期/Last Update: 2008-09-20