　ZHU Ya-chao,SONG Yu-pu,WANG Li-cheng.Experiment on Tension Softening Behavior of Mortar-aggregate Interface[J].Journal of Architecture and Civil Engineering,2011,28(01):91-95.
点击复制

砂浆-骨料界面拉伸软化性能试验(PDF)
分享到：

《建筑科学与工程学报》[ISSN:1673-2049/CN:61-1442/TU]

卷:
28卷
期数:
2011年01期
页码:
91-95
栏目:
出版日期:
2011-03-20

文章信息/Info

Title:
Experiment on Tension Softening Behavior of Mortar-aggregate Interface
作者:
朱亚超,宋玉普,王立成
大连理工大学 海岸和近海工程国家重点实验室,辽宁 大连 116024
Author(s):
ZHU Ya-chao, SONG Yu-pu, WANG Li-cheng
State Key Laboratory of Coastal and Offshore Engineering, Dalian University of Technology, Dalian 116024, Liaoning, China
关键词:
砂浆-骨料界面;  劈裂试验;  三点弯曲试验;  粗糙度;  断裂能;  拉伸软化曲线
Keywords:
mortar-aggregate interface;  splitting test;  three point bending test;  roughness;  fracture energy;  tension softening curve
分类号:
TU528.01
DOI:
-
文献标志码:
A
摘要:
对砂浆-骨料复合试件进行了劈裂试验和三点弯曲试验,基于试验结果和改进的J积分计算方法,提出了砂浆-骨料界面的拉伸软化曲线模型及其表达式。分析结果表明:砂浆基体的特性和粗骨料表面的粗糙度对砂浆-骨料界面的力学性能具有重要影响; 界面断裂能随着砂浆基体强度的提高和骨料表面粗糙度的提高而提高; 基体为普通强度砂浆的试件断裂多发生在界面附近的砂浆粘结层上; 基体为高强度砂浆的试件断裂多发生在砂浆粘结层和砂浆-骨料接合处的粘结层上。
Abstract:
Splitting tests and three point bending tests of mortar-aggregate composite specimens were carried out. Based on the test results and modified J-integral calculation method, tension softening curve model and its expression of mortar-aggregate interface were proposed. Analysis results indicate that the mortar matrix property and the roughness of aggregate interface have important effect on the mechanical properties of interface. The fracture energy of interface increases with the increasing of mortar matrix strength and aggregate surface roughness. The fracture interfaces of normal strength mortar specimens appear on the mortar joint interface, and the fracture interfaces of high strength mortar specimens appear on the mortar joint interface and mortar-aggregate interface.

参考文献/References:

[1] ZAITESV Y B,WITTMANN F H.Simulation of Crack Propagation and Failure of Concrete[J].Ma-terials and Structures,1981,14(5):357-365.
[2]王立成,陈桂斌.基于细观刚体弹簧元的轻骨料混凝土力学性能数值模拟[J].水利学报,2008,39(5):588-595. WANG Li-cheng,CHEN Gui-bin.Mesoscopic Simulation for Mechanical Properties of Lightweight Aggregate Concrete by Rigid Body Spring Model[J].Journal of Hydraulic Engineering,2008,39(5):588-595.
[3]马怀发,陈厚群,黎保琨.混凝土细观力学研究进展及评述[J].中国水利水电科学研究院学报,2004,2(2):124-130. MA Huai-fa,CHEN Hou-qun,LI Bao-kun.Review on Micro-mechanics Studies of Concrete[J].Journal of China Institute of Water Resources and Hydropower Research,2004,2(2):124-130.
[4]陈惠苏,孙 伟,STROEVEN P.水泥基复合材料集料与浆体界面研究综述(二):界面微观结构的形成、劣化机理及其影响因素[J].硅酸盐学报,2004,32(1):70-79. CHEN Hui-su,SUN Wei,STROEVEN P.Interfacial Transition Zone Between Aggregate and Paste in Cementitious Composites(Ⅱ):Mechanism of Formation and Degradation of Interfacial Transition Zone Microstructure,and Its Influence Factors[J].Journal of the Chinese Ceramic Society,2004,32(1):70-79.
[5]王 瑶,周继凯,沈德建,等.混凝土中骨料-浆体界面过渡区的力学性能研究综述[J].水利水电科技进展,2008,28(2):89-94. WANG Yao,ZHOU Ji-kai,SHEN De-jian,et al.Review of Study on Mechanical Property of Aggregate-mortar Interface Transitionzone of Concrete[J].Advances in Science and Technology of Water Resources,2008,28(2):89-94.
[6]ASTM C496-92,Standard Test Method for Splitting Tensile Strength of Cylindrical Concrete Specimens[S].
[7]RAMEY G E,STRICKLAND A M.An Experimental Evaluation of Rapid Setting Patching Materials Used in the Repair of Concrete Bridges and Pavements[R].New York:Alabama Highway Department,1984:48-56.
[8]HILLERBORG A,MODEER M,PETERSSON P E.Analysis of Crack Formation and Crack Growth in Concrete by Means of Fracture Mechanics and Finite Elements[J].Cement and Concrete Research,1976,6(6):773-781.
[9]RILEM Committe.Determination of the Fracture Energy of Mortar and Concrete by Means of Three Point Bend Tests on Notched Beams[J].Materials and Structures,1985,18(4):287-290.
[10]NIWA J,SUMRANWANICH T,TANTERMISIRIKUL S.New Method to Determine Tension Softening Curve of Concrete[C]//MIHASHI H,ROKUGO K.Fracture Mechanics of Concrete Structures.Freiburg:Aedificatio Publisher,1998:347-356.

相似文献/References:

[1]邢立坤,王立成,侯宇星.混凝土细观刚体弹簧元法在劈裂试验中的应用[J].建筑科学与工程学报,2011,28(01):83.
　XING Li-kun,WANG Li-cheng,HOU Yu-xing.Application of Mesoscopic Rigid-body-spring Method of Concrete in Splitting Test[J].Journal of Architecture and Civil Engineering,2011,28(01):83.

备注/Memo

备注/Memo:
收稿日期:2011-01-06
基金项目:国家自然科学基金重点项目(50838001); 国家自然科学基金重大研究计划项目(90815026); 教育部科学技术研究重点项目(109046)
作者简介:朱亚超(1987-),男,辽宁沈阳人,工学硕士研究生,E-mail:zhuyachao2006@163.com。
更新日期/Last Update: 2011-03-20