|本期目录/Table of Contents|

[1]王霄,陈志坚,徐钢.基于阳极梯系统的苏通大桥锚固区腐蚀监测研究[J].建筑科学与工程学报,2012,29(04):106-111.
　WANG Xiao,CHEN Zhi-jian,XU Gang.Research on Corrosion Monitoring in Anchorage Zone for Sutong Bridge Based on Anode-ladder System[J].Journal of Architecture and Civil Engineering,2012,29(04):106-111.
点击复制

基于阳极梯系统的苏通大桥锚固区腐蚀监测研究(PDF)
分享到：

《建筑科学与工程学报》[ISSN:1673-2049/CN:61-1442/TU]

卷:
29卷
期数:
2012年04期
页码:
106-111
栏目:
出版日期:
2012-12-30

文章信息/Info

Title:
Research on Corrosion Monitoring in Anchorage Zone for Sutong Bridge Based on Anode-ladder System
作者:
王霄1,陈志坚1,徐钢2
1. 河海大学 地球科学与工程学院,江苏 南京 210098; 2. 杭州园林设计院股份有限公司,浙江 杭州 310013
Author(s):
WANG Xiao1, CHEN Zhi-jian1, XU Gang2
1. School of Earth Sciences and Engineering, Hohai University, Nanjing 210098, Jiangsu, China; 2. Hangzhou Landscape Architecture Design Institute Co. Ltd., Hangzhou 310013, Zhejiang, China
关键词:
阳极梯系统;  苏通大桥;  干湿交替循环;  锚固区;  腐蚀监测;  质量损失
Keywords:
anode-ladder system;  Sutong Bridge;  wet-dry cycling;  anchorage zone;  corrosion monitoring;  mass loss
分类号:
U445.7
DOI:
-
文献标志码:
A
摘要:
对腐蚀的发生机理和影响因素进行了概括,介绍了基于宏腐蚀原理开发的阳极梯系统的工作原理和评价体系; 鉴于阳极梯系统难以捕捉到腐蚀发生时的微电流,运用法拉第第二定律计算钢筋锈蚀质量损失存在较大误差,因此采用干湿循环交替试验修正了混凝土开裂后锈蚀质量损失与宏电流的函数关系; 根据苏通大桥索塔锚固区的实测数据,简要评估了当前索塔塔壁混凝土碳化程度和钢筋的腐蚀状态。结果表明:索塔锚固区混凝土不同深度的电位及电阻率变化较为稳定,腐蚀宏电流曲线相对平稳,宏电流极值远小于耦合电流的临界值15 μA,锚固区混凝土的碳化速度缓慢,钢筋尚未发生腐蚀。研究结果可为相关桥梁结构腐蚀监测提供一定的参考。
Abstract:
The corrosion mechanism and the influence factors were summarized, and the working principle of anode-ladder system, which was developed based on the macro corrosion, was introduced in details. The anode-ladder system could hardly catch the micro current, which resulted in large errors when the Faraday's Second Law was used, to calculate the mass loss caused by corrosion of steel bar. The functional relation between macro current and the mass loss was fixed through wet-dry cycling experiment. According to the measured data in anchorage zone for Sutong Bridge, the current carbonization degree of concrete and the corrosion state of steel bar in cable tower could be assessed.The results show that the cable tower anchorage zone concrete potential and resistivity change in different depths is relatively stable, macro corrosion current curve is relatively smooth, macro current extremum is far less than the critical value of the coupling current about 15 μA, the rate of concrete carbonization is relatively slow in anchorage zone, and the corrosion of steel bar has not occurred.The research can provide some references for the corrosion monitoring in correlation bridge structures.

参考文献/References:

[1] BA M F,QIAN C X,HUANG L.Probabilistic Method and Its Application for Evaluating Carbonation Life of Newly-built Concrete Structures[J].Journal of Southeast University:English Edition,2010,26(4):578-581.
[2]GONZALEZ J A,FELIU S,RODRIGUEZ P,et al.Some Questions on the Corrosion of Steel in Concrete.PartⅡ:Corrosion Mechanism and Monitoring,Service Life Prediction and Protection Methods[J].Materials and Structures,1996,29(2):97-104.
[3]邸小坛,周 燕.旧建筑物的监测加固与维护[M].北京:地震出版社,1992. DI Xiao-tan,ZHOU Yan.Monitoring and Maintaining of the Old Building[M].Beijing:Earthquake Press, 1992.
[4]干伟忠,RAUPACH M,金伟良,等.杭州湾跨海大桥混凝土结构耐久性原位监测预警系统[J].中国公路学报,2010,23(2):30-35. GAN Wei-zhong,RAUPACH M,JIN Wei-liang,et al.In-situ Monitoring and Early Warning System for Durability of Concrete Structure of Hangzhou Bay Sea-crossing Bridge[J].China Journal of Highway and Transport,2010,23(2):30-35.
[5]金 晶.腐蚀监测子系统在苏通大桥中的应用[J].中国科技信息,2010(9):53-57. JIN Jin.The Application of Corrosion Subsystem for Sutong Bridge[J].China Science and Technology Information,2010(9):53-57.
[6]何谋杰,叶跃忠,李福海.预埋式阳极梯监测系统研究[J].材料导报,2010,24(12):79-82. HE Mou-jie,YE Yue-zhong,LI Fu-hai.Research on the Anode-ladder Monitoring System[J].Materials Review,2010,24(12):79-82.
[7]赵 卓,蒋晓东.受腐蚀混凝土结构耐久性检测诊断[M].郑州:黄河水利出版社,2006. ZHAO Zhuo,JIANG Xiao-dong.Testing and Diagnosing the Corrosion Concrete Durability[M].Zhengzhou:Yellow River Water Conservancy Press,2006.
[8]杨绮琴,方北龙,童叶翔.应用电化学[M].2版.广州:中山大学出版社,2005. YANG Qi-qin,FANG Bei-long,TONG Ye-xiang.Applied Electrochemistry[M].2nd ed.Guangzhou:Zhongshan University Press,2005.
[9]李富民,袁迎曙,耿 欧,等.混凝土中钢筋腐蚀速率的理论模型[J].华南理工大学学报:自然科学版,2009,37(8):83-88. LI Fu-min,YUAN Ying-shu,GENG Ou,et al.Theoretical Models of Corrosion Rate of Steel Bars Embedded in Concrete[J].Journal of South China University of Technology:Nature Science Edition,2009,37(8):83-88.
[10]延永东.氯离子在损伤及开裂混凝土内的输运机理及作用效应[D].杭州:浙江大学,2011. YAN Yong-dong.Transportation of Chloride Ions in Damaged and Cracked Concrete and Its Action[D].Hangzhou:Zhejiang University,2011.
[11]柳俊哲,太星镐,野口贵文.掺防冻剂混凝土中亚硝酸盐的长期阻锈效果[J].混凝土,2004(9):14-17. LIU Jun-zhe,TAI Sun-gho,TAKAFUMI Noguchi.Study on Long Term Inhibiting Effectiveness of Nitrite Ion in Concrete Mixed with Anti-freezing Admixtures[J].Concrete,2004(9):14-17.
[12]金伟良,赵羽习.混凝土结构耐久性[M].北京:科学出版社,2002:93-96. JIN Wei-liang,ZHAO Yu-xi.The Concrete Structure Durability[M].Beijing:Science Press,2002:93-96.
[13]牛荻涛,陈亦奇,于 澍.混凝土结构的碳化模式与碳化寿命分析[J].西安建筑科技大学学报:自然科学版,1995,27(4):365-369. NIU Di-tao,CHEN Yi-qi,YU Shu.Model and Reliability Analysis for Carbonation of Concrete Structures[J].Journal of Xi'an University of Architecture & Technology:Natural Science Edition,1995,27(4):365-369.

相似文献/References:

备注/Memo

备注/Memo:
收稿日期:2012-08-07
基金项目:江苏省交通科学研究规划课题资助项目(08Y60)
作者简介:王 霄(1987-),男,云南昭通人,工学硕士研究生,E-mail:xxx1254@126.com。
更新日期/Last Update: 2012-12-20