Title:

Mechanical properties and microstructure of fiber reinforced geopolymer concrete

文章编号:

1673-2049(2023)04-0012-12

作者:

黄 华^1,2,郭梦雪¹,于基宁³,杨世林¹

(1. 西安工业大学 建筑工程学院,陕西 西安 710021; 2. 长安大学 建筑工程学院,陕西 西安 710061; 3. 中铁第一勘察设计院集团有限公司,陕西 西安 710043)

Author(s):

HUANG Hua^1,2, GUO Mengxue¹, YU Jining³, YANG Shilin¹

(1. School of Civil & Architecture Engineering, Xi'an Technological University, Xi'an 710021, Shaanxi, China; 2. School of Civil Engineering, Chang'an University, Xi'an 710061, Shaanxi, China; 3. China Railway First Survey and Design Institute Group Co., Ltd., Xi'an 710043, Shaanxi, China)

关键词:

地聚物混凝土;  纤维增韧;  力学性能;  微观结构;  整体式纤维;  层布式纤维

Keywords:

geopolymer concrete;  fiber reinforcement;  mechanical property;  microstructure;  non-layered fiber;  layered fiber

分类号:

TU375.3

DOI:

10.19815/j.jace.2021.12014

文献标志码:

A

摘要:

为改善地聚物延性较差的缺点,采用镀铜微细钢纤维与聚丙烯纤维制备了不同纤维类型、布置形式与体积掺量的纤维增韧粉煤灰-矿渣基地聚物混凝土,对其力学性能进行了试验研究,并通过扫描电子显微镜从微观层面解释了不同布置形式的纤维增韧机理。结果表明:钢纤维与聚丙烯纤维分别以拔出与断裂的形式有效地阻止地聚物混凝土裂缝的发展; 对于整体式单掺钢纤维与整体式混掺纤维地聚物混凝土试样,其劈裂抗拉强度与抗折强度均得到显著提升; 层布式钢纤维地聚物混凝土试样可达到与整体式纤维地聚物混凝土相当的力学性能且前者的纤维用量仅为后者的40%左右; 与整体式纤维增韧机理不同,层布式钢纤维地聚物混凝土试样中双层钢纤维相当于“双层弹性板”,除了聚丙烯纤维以及钢纤维的“桥接”作用,还可与基体周围的钢纤维互相交叉形成网状结构,钢纤维网状结构之间的相互作用限制了纤维的相对位移,显著提升了试样的力学性能。

Abstract:

To improve the poor ductility of geopolymer, fiber reinforced fly ash-slag geopolymer concrete with different fiber types, arrangement forms and volume content was prepared by using copper coated micro steel fiber and polypropylene fiber. The mechanical properties of geopolymer concrete were studied, and the fiber reinforcement mechanism with different arrangement forms was further explained based on scanning electron microscope. The results show that steel fiber and polypropylene fiber can effectively prevent the development of cracks in geopolymer concrete in the form of pull-out and fracture, respectively. The splitting tensile and flexural strength of non-layered reinforced geopolymer concrete samples with single steel fiber and hybrid fiber are significantly improved. The mechanical properties of layered fiber reinforced geopolymer concrete are equivalent to that of non-layered fiber reinforced geopolymer concrete, and the fiber content of the former is only about 40% of that of the latter. Different from the non-layered fiber reinforced mechanism, the double-layer steel fiber in the layered fiber reinforced geopolymer concrete is equivalent to the “double-layer elastic plate”. Besides the “bridging” effect of polypropylene fiber and steel fiber, it also intersects with the steel fiber around the matrix to form a network structure. The interaction between the steel fiber network structure limits the relative displacement of the fiber and significantly improves the mechanical properties of the sample.

参考文献/References:

[1] DUXSON P,PROVIS J L,LUKEY G C,et al.The role of inorganic polymer technology in the development of ‘green concrete'[J].Cement and Concrete Research,2007,37(12):1590-1597.
[2]LV Q F,WANG Z S,GU L Y,et al.Effect of sodium sulfate on strength and microstructure of alkali-activated fly ash based geopolymer[J].Journal of Central South University,2020,27(6):1691-1702.
[3]BAI C Y,COLOMBO P.Processing,properties and applications of highly porous geopolymers:a review[J].Ceramics International,2018,44(14):16103-16118.
[4]SETHU P S,SHARMA A K,ANAND K B.Comparative study on synthesis and properties of geopolymer fine aggregate from fly ashes[J].Construction and Building Materials,2019,198:359-367.
[5]NAGHIZADEH A,EKOLU S O.Method for comprehensive mix design of fly ash geopolymer mortars[J].Construction and Building Materials,2019,202:704-717.
[6]YAN S,HE P G,JIA D C,et al.Effects of high-temperature heat treatment on the microstructure and mechanical performance of hybrid C_f-SiC_f-(Al₂O_3p)reinforced geopolymer composites[J].Composites Part B:Engineering,2017,114:289-298.
[7]YE J Y,ZHANG W S,SHI D.Performance evolutions of tailing-slag-based geopolymer under severe conditions[J].Journal of Sustainable Cement-Based Materials,2015,4(2):101-115.
[8]GHOLAMPOUR A,HO V D,OZBAKKALOGLU T.Ambient-cured geopolymer mortars prepared with waste-based sands:mechanical and durability-related properties and microstructure[J].Composites Part B:Engineering,2019,160:519-534.
[9]罗 为,熊光启,熊晨晨,等.振动搅拌工艺制备轻质高强钢纤维混凝土[J].中南大学学报(自然科学版),2020,51(1):14-22.
LUO Wei,XIONG Guangqi,XIONG Chenchen,et al.Preparation of steel fiber reinforced high strength lightweight concrete using vibration mixing technology[J].Journal of Central South University(Science and Technology),2020,51(1):14-22.
[10]MOHSENI E,DANIEL TSAVDARIDIS K.Effect of nano-alumina on pore structure and durability of class F fly ash self-compacting mortar[J].American Journal of Engineering and Applied Sciences,2016,9(2):323-333.
[11]梁宁慧,钟 杨,刘新荣.多尺寸聚丙烯纤维混凝土抗弯韧性试验研究[J].中南大学学报(自然科学版),2017,48(10):2785-2791.
LIANG Ninghui,ZHONG Yang,LIU Xinrong.Experimental study of flexural toughness for multi-scale polypropylene fiber reinforced concrete[J].Journal of Central South University(Science and Technology),2017,48(10):2785-2791.
[12]BERNAL S,DE GUTIERREZ R,DELVASTO S,et al.Performance of an alkali-activated slag concrete reinforced with steel fibers[J].Construction and Building Materials,2010,24(2):208-214.
[13]SHAIKH F U A.Review of mechanical properties of short fibre reinforced geopolymer composites[J].Construction and Building Materials,2013,43:37-49.
[14]HA K,CHOI H,SHIN M,et al.On the size effect of interfacial fracture between concrete and fiber reinforced polymer[J].Cement and Concrete Composites,2018,93:99-106.
[15]DEEPA RAJ S,RAMACHANDRAN A.Performance of hybrid fibre reinforced geopolymer concrete beams[J].SN Applied Sciences,2019,1(12):1-8.
[16]KHERADMAND M,MASTALI M,ABDOLLAHNEJAD Z,et al.Experimental and numerical investigations on the flexural performance of geopolymers reinforced with short hybrid polymeric fibres[J].Composites Part B:Engineering,2017,126:108-118.
[17]NOUSHINI A,HASTINGS M,CASTEL A,et al.Mechanical and flexural performance of synthetic fibre reinforced geopolymer concrete[J].Construction and Building Materials,2018,186:454-475.
[18]ANJBAR N,TALEBIAN M,MEHRALI M,et al.Mechanisms of interfacial bond in steel and polypropylene fiber reinforced geopolymer composites[J].Composites Science and Technology,2016,122:73-81.
[19]JEWELL R B,MAHBOUB K C,ROBL T L,et al.Interfacial bond between reinforcing fibers and calcium sulfoaluminate cements:fiber pullout characteristics[J].ACI Materials Journal,2015,112(1):39-48.
[20]纤维混凝土结构技术规程:CECS 38:2004[S].北京:中国计划出版社,2005.
Technical specification for fiber reinforced concrete structures:CECS 38:2004[S].Beijing:China Planning Press,2005.
[21]混凝土物理力学性能试验方法标准:GB/T 50081—2019[S].北京:中国建筑工业出版社,2019.
Standard for test methods of concrete physical and mechanical properties:GB/T 50081—2019[S].Beijing:China Architecture & Building Press,2019.
[22]混凝土强度检验评定标准:GB/T 50107—2010[S].北京:中国建筑工业出版社,2010.
Standard for evaluation of concrete compressive strength:GB/T 50107—2010[S].Beijing:China Architecture & Building Press,2010.
[23]GUO L,WU Y Y,XU F,et al.Sulfate resistance of hybrid fiber reinforced metakaolin geopolymer composites[J].Composites Part B:Engineering,2020,183:107689.
[24]SUN W,MANDEL J A,SAID S.Study of the interface strength in steel fiber-reinforced cement-based composites[J].ACI Journal Proceedings,1986,83(4):597-605.
[25]AL-MASHHADANI M M,CANPOLAT O,AYGORMEZ Y,et al.Mechanical and microstructural characterization of fiber reinforced fly ash based geopolymer composites[J].Construction and Building Materials,2018,167:505-513.
[26]RANJBAR N,MEHRALI M,MEHRALI M,et al.Graphene nanoplatelet-fly ash based geopolymer composites[J].Cement and Concrete Research,2015,76:222-231.
[27]PAYAKANITI P,PINITSOONTORN S,THONGBAI P,et al.Electrical conductivity and compressive strength of carbon fiber reinforced fly ash geopolymeric composites[J].Construction and Building Materials,2017,135:164-176.
[28]张 华,郜余伟,李 飞,等.高应变率下聚丙烯纤维混凝土动态力学性能和本构模型[J].中南大学学报(自然科学版),2013,44(8):3464-3473.
ZHANG Hua,GAO Yuwei,LI Fei,et al.Experimental study on dynamic properties and constitutive model of polypropylene fiber concrete under high strain rate[J].Journal of Central South University(Science and Technology),2013,44(8):3464-3473.

相似文献/References:

备注/Memo

备注/Memo:

收稿日期:2022-12-23
基金项目:国家自然科学基金项目(51708060); 陕西省杰出青年科学基金项目(2023-JC-JQ-47)
作者简介:黄 华(1979-),男,工学博士,教授,博士生导师,E-mail:huanghua23247@163.com。

常用功能

更新日期/Last Update: 2023-07-01