Title:

Bending fatigue characteristics of frozen-thawed basalt fiber recycled concrete

文章编号:

1673-2049(2023)01-0014-07

作者:

侯永利^1,2,俞正兴¹,周磊磊³,吕东朔¹

(1. 内蒙古工业大学 土木工程学院,内蒙古 呼和浩特 010051; 2. 内蒙古工业大学 内蒙古自治区建筑检测鉴定与安全评估工程技术研究中心,内蒙古 呼和浩特 010051; 3. 山西四建集团有限公司,山西 太原 030012)

Author(s):

HOU Yongli^1,2,YU Zhengxing¹,ZHOU Leilei³, LYU Dongshuo¹

(1. School of Civil Engineering, Inner Mongolia University of Technology, Hohhot 010051, Inner Mongolia, China; 2. Inner Mongolia Autonomous Region Building Inspection Appraisal and Safety Assessment Engineering Technology Research Center, Inner Mongolia University of Technology, Hohhot 010051, Inner Mongolia, China; 3. China Shanxi Sijian Group Co., Ltd, Taiyuan 030012, Shanxi, China)

关键词:

再生混凝土;  玄武岩纤维;  冻融循环;  疲劳寿命;  疲劳方程

Keywords:

recycled concrete;  basalt fiber;  freeze-thaw cycle;  fatigue life;  fatigue equation

分类号:

TU502

DOI:

10.19815/j.jace.2021.09007

文献标志码:

A

摘要:

基于中国北方地区气候特点及混凝土路面的受力特征,研究冻融损伤对玄武岩纤维再生混凝土(BFRC)弯曲疲劳特性的影响。首先对BFRC采用快冻法进行冻融循环试验,研究BFRC的冻融损伤形貌、质量、相对动弹性模量和相对抗折强度的变化; 然后针对经历不同冻融循环次数后BFRC的弯曲疲劳特性进行了试验研究,分析了冻融循环次数与应力水平对BFRC疲劳寿命的影响规律; 最后基于两参数Weibull分布理论对BFRC的疲劳寿命进行分析,预测了不同失效概率下的疲劳寿命并建立了失效概率为0.05和0.5下的双对数疲劳方程。结果表明:随着冻融循环次数的增加,试件表面损伤程度和质量损失率逐渐增大,相对动弹性模量和相对抗折强度逐渐下降,当冻融循环达到225次时,BFRC的相对动弹性模量和相对抗折强度与冻融循环前相比分别下降了12.4%和35.1%; 随着冻融循环次数和应力水平的增加,弯曲疲劳寿命逐渐减小; BFRC经冻融循环后的弯曲疲劳寿命服从两参数Weibull分布,失效概率为0.5的预测疲劳寿命与试验所得平均疲劳寿命十分接近; 建立的双对数疲劳方程能较好地反映冻融后BFRC应力水平S与疲劳寿命N之间的关系,研究成果为BFRC在路面结构中的安全应用提供可靠依据。

Abstract:

Based on the climatic characteristics of northern China and the mechanical characteristics of concrete pavement, the influence of freeze-thaw damage on the bending fatigue characteristics of basalt fiber recycled concrete(BFRC)was investigated. Firstly, the fast freezing method was used in the freeze-thaw cycle test of BFRC to investigate the changes of freeze-thaw damage morphology, mass, relative dynamic elastic modulus and relative flexural strength of BFRC. Then, the bending fatigue properties of BFRC after different freeze-thaw cycles were investigated by experiment, and the influence of freeze-thaw cycles and stress levels on the fatigue life of BFRC was analyzed. Finally, the fatigue life of BFRC was analyzed based on two-parameter Weibull distribution theory. The fatigue life of BFRC with different failure probability was predicted and the double logarithmic fatigue equations with failure probability of 0.05 and 0.5 were established. The results show that with the increase of the freeze-thaw cycles, the damage degree of specimen surface and the mass loss rate increase gradually, and the relative dynamic elastic modulus and relative flexural strength decrease gradually. When the times of freeze-thaw cycle reach 225, the relative dynamic elastic modulus and relative flexural strength of BFRC decrease by 12.4% and 35.1% respectively compared with those before freeze-thaw cycle. With the increase of freeze-thaw cycle and stress level, bending fatigue life decreases gradually. The bending fatigue life of freeze-thawed BFRC obeys two-parameter Weibull distribution. The predicted fatigue life with failure probability of 0.5 is very close to the average fatigue life obtained by test. The established double logarithmic fatigue equation can well reflect the relationship between stress level S and fatigue life N of frozen-thawed BFRC. The research findings provide a reliable basis for the safe application of BFRC in pavement structure.

参考文献/References:

[1] 张 娜,周 健,徐名凤,等.玄武岩纤维高延性水泥基复合材料的动态力学性能[J].爆炸与冲击,2020,40(5):45-53.
ZHANG Na,ZHOU Jian,XU Mingfeng,et al.Dynamic mechanical properties of basalt fiber engineered cementitious composites[J].Explosion and Shock Waves,2020,40(5):45-53.
[2]李 飞,陈鲤波,马建宁,等.玄武岩-聚乙烯醇混杂纤维水泥基材料的耐久性研究[J].功能材料,2020,51(3):3139-3143.
LI Fei,CHEN Libo,MA Jianning,et al.Study on durability of basalt-polyvinyl alcohol hybrid fiber cement-based materials[J].Journal of Functional Materials,2020,51(3):3139-3143.
[3]BRANSTON J,DAS S,KENNO S Y,et al.Mechanical behaviour of basalt fibre reinforced concrete[J].Construction and Building Materials,2016,124:878-886.
[4]DONG J F,WANG Q Y,GUAN Z W.Material properties of basalt fibre reinforced concrete made with recycled earthquake waste[J].Construction and Building Materials,2017,130:241-251.
[5]DEBIEB F,COURARD L,KENAI S,et al.Mechanical and durability properties of concrete using contaminated recycled aggregates[J].Cement and Concrete Composites,2010,32(6):421-426.
[6]RICHARDSON A,COVENTRY K,BACON J.Freeze/thaw durability of concrete with recycled demolition aggregate compared to virgin aggregate concrete[J].Journal of Cleaner Production,2011,19(2/3):272-277.
[7]姚烈波.粉煤灰品质和取代率对再生混凝土抗冻性能影响[J].重庆建筑,2019,18(3):43-46.
YAO Liebo.Influence of quality and substitution rate of fly ash on anti-freeze performance of recycled coarse aggregate concrete[J].Chongqing Architecture,2019,18(3):43-46.
[8]吴瑾炎,李碧雄,王燕鹏,等.添加粉煤灰和硅粉的路面高性能再生混凝土冻融特性试验研究[J].混凝土,2014(4):66-69,73.
WU Jinyan,LI Bixiong,WANG Yanpeng,et al.Study on the freeze-thaw test of high-performance recycled concrete mixed with fly ash and silica fume used for pavement[J].Concrete,2014(4):66-69,73.
[9]张云飞,刘元珍,张泽平,等.再生保温混凝土冻融循环后抗压强度影响因素研究[J].中国科技论文,2016,11(9):1027-1030.
ZHANG Yunfei,LIU Yuanzhen,ZHANG Zeping,et al.Influence of experimental factor on compressive strength of recycled aggregate thermal insulation concrete after freeze-thaw Cycle[J].China Sciencepaper,2016,11(9):1027-1030.
[10]陈彦文,潘文浩,孙小巍.预处理再生骨料混凝土性能的试验研究[J].混凝土,2012(1):81-83.
CHEN Yanwen,PAN Wenhao,SUN Xiaowei.Performance study of pretreated concrete with recycled aggregate[J].Concrete,2012(1):81-83.
[11]王玲玲,陈彦文,潘文浩,等.制备工艺对再生混凝土耐久性影响研究[J].混凝土,2012(11):142-144.
WANG Lingling,CHEN Yanwen,PAN Wenhao,et al.Effects of manufacture technology on durability of recycled concrete[J].Concrete,2012(11):142-144.
[12]SAINI B S,SINGH S P.Flexural fatigue life analysis of self compacting concrete containing 100% coarse recycled concrete aggregates[J].Construction and Building Materials,2020,253:119176.
[13]LI W Z,CAI L C,WU Y G,et al.Assessing recycled pavement concrete mechanical properties under joint action of freezing and fatigue via RSM[J].Construction and Building Materials,2018,164:1-11.
[14]欧祖敏,孙 璐.冻融损伤混凝土的弯曲疲劳寿命可靠性分析[J].浙江大学学报(工学版),2017,51(6):1074-1081,1103.
OU Zumin,SUN Lu.Flexural fatigue-life reliability of frost-damaged concrete[J].Journal of Zhejiang University(Engineering Science),2017,51(6):1074-1081,1103.
[15]李召行.荷载与腐蚀冻融耦合及再生粗骨料性能对再生混凝土耐久性能的影响研究[D].南昌:南昌大学,2019.
LI Zhaohang.Research on the influence of coupling multi-factors of load and corrosion freeze-thaw and recycled coarse aggregate on durability of recycled concrete[D].Nanchang:Nanchang University,2019.
[16]HASAN M,UEDA T,SATO Y.Stress-strain relationship of frost-damaged concrete subjected to fatigue loading[J].Journal of Materials in Civil Engineering,2008,20(1):37-45.
[17]齐振麟.冻融损伤后再生混凝土单调及重复荷载下本构关系研究[D].哈尔滨:哈尔滨工业大学,2016.
QI Zhenlin.Study on constitutive relation of recycled aggregate concrete damaged by freeze-thaw under monotic and cyclic loading[D].Harbin:Harbin Institute of Technology,2016.

相似文献/References:

[1]丁发兴,方常靖,龚永智,等.再生混凝土单轴力学性能指标统一计算方法[J].建筑科学与工程学报,2014,31(04):16.
　DING Fa-xing,FANG Chang-jing,GONG Yong-zhi,et al.Unified Calculation Method of Uniaxial Mechanical Performance Index of Recycled Concrete[J].Journal of Architecture and Civil Engineering,2014,31(01):16.
[2]丁 陶,肖建庄.基于振动台试验的预制再生混凝土框架后浇边节点分析[J].建筑科学与工程学报,2013,30(03):78.
　DING Tao,XIAO Jian-zhuang.Analysis of Cast-in-situ Exterior Joints of Precast Recycled Aggregate Concrete Frame by Shaking Table Tests[J].Journal of Architecture and Civil Engineering,2013,30(01):78.
[3]肖建庄,郑世同,王 静.再生混凝土长龄期强度与收缩徐变性能[J].建筑科学与工程学报,2015,32(01):21.
　XIAO Jian-zhuang,ZHENG Shi-tong,WANG Jing.Long-term Strength, Shrinkage and Creep Properties of Recycled Aggregate Concrete[J].Journal of Architecture and Civil Engineering,2015,32(01):21.
[4]肖建庄,刘 胜,TRESSERRAS Joan.钢管/GFRP管约束再生混凝土柱偏心受压试验[J].建筑科学与工程学报,2015,32(02):21.
　XIAO Jian-zhuang,LIU Sheng,TRESSERRAS Joan.Eccentric Loading Test on Recycled Aggregate Concrete Columns Confined by Steel Tube/GFRP Tube[J].Journal of Architecture and Civil Engineering,2015,32(01):21.
[5]谢建和,李自坚,孙明炜.硅粉对纤维橡胶再生混凝土抗压性能影响试验[J].建筑科学与工程学报,2016,33(03):72.
　XIE Jian-he,LI Zi-jian,SUN Ming-wei.Experiment About Influence of Silica Fume on Compressive Performance of Fiber Reinforced Rubber Recycled Concrete[J].Journal of Architecture and Civil Engineering,2016,33(01):72.
[6]肖建庄,李宏,亓萌.基于静载强度分布的再生混凝土疲劳强度预测[J].建筑科学与工程学报,2010,27(04):7.
　XIAO Jian-zhuang,LI Hong,QI Meng.Fatigue Strength Prediction of Recycled Aggregate ConcreteBased on Static Strength Distribution[J].Journal of Architecture and Civil Engineering,2010,27(01):7.
[7]肖建庄,朱永明,王璞瑾,等.再生混凝土U型叠合梁抗剪性能[J].建筑科学与工程学报,2012,29(02):1.
　XIAO Jian-zhuang,ZHU Yong-ming,WANG Pu-jin,et al.Shear Behavior of Recycled Concrete U-shaped Composite Beams[J].Journal of Architecture and Civil Engineering,2012,29(01):1.
[8]肖建庄,黄运标,郑永朝.高温后再生混凝土的残余抗折强度[J].建筑科学与工程学报,2009,26(03):32.
　XIAO Jian-zhuang,HUANG Yun-biao,ZHENG Yong-chao.Residual Flexural Strength of Recycled ConcreteAfter Elevated-temperatures[J].Journal of Architecture and Civil Engineering,2009,26(01):32.
[9]肖建庄,雷斌.再生混凝土碳化模型与结构耐久性设计[J].建筑科学与工程学报,2008,25(03):66.
　XIAO Jian-zhuang,LEI Bin.Carbonation Model and Structural Durability Design for Recycled Concrete[J].Journal of Architecture and Civil Engineering,2008,25(01):66.
[10]郭 凯,马浩辉,王 强.氧化石墨烯对再生混凝土界面过渡区的影响[J].建筑科学与工程学报,2018,35(05):217.
　GUO Kai,MA Hao-hui,WANG Qiang.Effect of Graphene Oxide on Interfacial Transition Zone of Recycled Concrete[J].Journal of Architecture and Civil Engineering,2018,35(01):217.

备注/Memo

备注/Memo:

收稿日期:2021-09-13
基金项目:内蒙古自治区自然科学基金项目(2019MS05023); 中央引导地方科技发展资金项目(2022ZY0189)
作者简介:侯永利(1972-),男,工学博士,副教授,E-mail:houyongli@imut.edu.cn。

常用功能

更新日期/Last Update: 2023-01-01