«上一篇/Previous Article|本期目录/Table of Contents|下一篇/Next Article»

《建筑科学与工程学报》[ISSN:1673-2049/CN:61-1442/TU]

卷:

41卷

期数:

2024年03期

页码:

26-33

栏目:

建筑材料

出版日期:

2024-05-20

文章信息/Info

Title:

Study on properties of C50 concretes with match curing based on entity temperature of mass concrete for bridge cable tower

文章编号:

1673-2049(2024)03-0026-08

作者:

杨宏天¹,李北星¹,田常兵²,钟 翔¹

(1. 武汉理工大学 硅酸盐建筑材料国家重点实验室,湖北 武汉 430070; 2. 湖北嘉鱼长江公路大桥有限公司,湖北 咸宁 430051)

Author(s):

YANG Hongtian¹, LI Beixing¹, TIAN Changbing², ZHONG Xiang¹

(1. State Key Laboratory of Silicate Materials for Architectures, Wuhan University of Technology, Wuhan 430070, Hubei, China; 2. Hubei Jiayu Yangtze River Highway Bridge Co., Ltd., Xianning 430051, Hubei, China)

关键词:

养护温度;  索塔;  矿物掺合料;  强度;  抗氯离子渗透性;  水化

Keywords:

curing temperature;  cable tower;  mineral admixture;  strength;  resistance to chloride ion penetration;  hydration

分类号:

TU528

DOI:

10.19815/j.jace.2022.05004

文献标志码:

A

摘要:

为探究桥梁索塔结构内部混凝土的实际性能发展规律,将某长江公路大桥索塔C50大体积混凝土施工时的芯部温度作为混凝土的匹配养护温度,对比研究了标准养护和温度匹配养护对纯水泥、单掺20%粉煤灰、复掺20%粉煤灰和15%矿粉3种C50混凝土试件的强度发展规律、抗氯离子渗透性和水化产物微观形貌的影响。结果表明:温度匹配养护下的高水化温度显著激发了掺有粉煤灰和矿粉的复合胶凝材料的水化活性,复掺粉煤灰和矿粉的混凝土在温度匹配养护下的3 d抗压强度和抗折强度较标准养护分别提高45%和30%以上; 温度匹配养护抑制了纯水泥混凝土的后期强度发展,且增大了其脆性,降低了抗氯离子渗透性,而单掺粉煤灰或复掺粉煤灰和矿粉可以改善或消除上述不利影响; 无论是标准养护还是温度匹配养护,复掺粉煤灰和矿粉的混凝土具有最高强度、最大折压比和最好的抗氯离子渗透性,适合索塔大体积混凝土结构施工使用。

Abstract:

In order to explore the development law of the actual performance of concrete for the bridge cable tower structure,the core temperature of C50 mass concrete construction of the cable tower of a Yangtze River highway bridge was used as the matching curing temperature of concrete. The effects of standard curing and temperature matching curing on the strength development law, resistance to chloride ion permeability and microstructure of hydration products of three kinds of C50 concrete specimens of pure cement, addition of 20% fly ash(FA), mixed with 20% FA and 15% ground granular blast furnace slag(GGBS)were compared and studied. The results show that the high hydration temperature under the temperature matching curing significantly stimulates the hydration activity of the composite cementitious material mixed with FA and GGBS. The 3 d compressive strength and flexural strength of the concrete mixed with FA and GGBS under temperature matching curing condition are increased by more than 45% and 30% respectively than those under standard curing condition. Temperature matching curing inhibits the later strength development of pure cement concrete, increases its brittleness and reduces its resistance to chloride ion permeability, and the above adverse effects can be improved or eliminated by addition of FA or mixed FA and GGBS. Whether under standard curing or temperature matching curing, the concrete mixed with FA and GGBS has the highest strength, the maximum ratio of folding pressure and the best resistance to chloride ion penetration, which is suitable for the construction of mass concrete structure of cable tower.

参考文献/References:

[1] 纪登贵,肖 义.索塔实心段高强度大体积混凝土施工控裂技术研究及效果评价[J].建筑安全,2017,32(12):4-8.
JI Denggui,XIAO Yi.Research and effect evaluation of crack control technology for high strength mass concrete construction in solid section of cable tower[J].Construction Safety,2017,32(12):4-8.
[2]王 涛.嘉鱼长江公路大桥主墩混凝土配制及防裂技术研究[D].武汉:武汉理工大学,2017.
WANG Tao.Research on preparation and crack control technology of main pier concrete in Jiayu Yangtze River highway bridge[D].Wuhan:Wuhan University of Technology,2017.
[3]周乾大,魏剑峰.安九铁路鳊鱼洲长江大桥桥塔防裂技术[J].世界桥梁,2022,50(1):40-45.
ZHOU Qianda,WEI Jianfeng.Pylon anti-cracking techniques for Bianyuzhou Changjiang River bridge of Anqing-Jiujiang railway[J].World Bridges,2022,50(1):40-45.
[4]徐 文,闫志刚,张士山,等.沪通长江大桥主航道桥桥塔温度场与膨胀调控抗裂技术[J].桥梁建设,2020,50(1):44-49.
XU Wen,YAN Zhigang,ZHANG Shishan,et al.Technique of controlling temperature field and concrete expansion to limit cracking in pylons of main navigational channel bridge of Hutong Changjiang River bridge[J].Bridge Construction,2020,50(1):44-49.
[5]马春生,王 萍.某大桥桥塔裂缝成因分析[J].公路,2002,47(8):44-47.
MA Chunsheng,WANG Ping.Analysis of crack causes of certain bridge tower[J].Highway,2002,47(8):44-47.
[6]成文佳,强士中,夏招广.重庆李家沱长江大桥裂缝成因分析与对策[J].四川建筑,2005,25(3):81-83.
CHENG Wenjia,QIANG Shizhong,XIA Zhaoguang.Cause analysis and countermeasures of cracks in Lijiatuo Yangtze River bridge in Chongqing[J].Sichuan Architectural,2005,25(3):81-83.
[7]甘应朋.夷陵大桥斜拉桥主塔下塔柱裂缝分析与处理[J].交通科技,2004(3):51-53.
GAN Yingpeng.Analysis and treatment of cracks in tower column under main tower of cable-stayed bridge of Yiling bridge[J].Transportation Science & Technology,2004(3):51-53.
[8]徐小华,谢俊凡,夏伟航,等.矿物掺合料对桥塔混凝土性能与微结构的影响[J].中国港湾建设,2021,41(2):40-45.
XU Xiaohua,XIE Junfan,XIA Weihang,et al.Influence of mineral admixtures on performance and microstructure of bridge tower concrete[J].China Harbour Engineering,2021,41(2):40-45.
[9]LOTHENBACH B,WINNEFELD F,ALDER C,et al.Effect of temperature on the pore solution,microstructure and hydration products of Portland cement pastes[J].Cement and Concrete Research,2007,37(4):483-491.
[10]KJELLSEN K O,DETWILER R J,GJORV O E.Development of microstructures in plain cement pastes hydrated at different temperatures[J].Cement and Concrete Research,1991,21(1):179-189.
[11]AL-GAHTANI A S.Effect of curing methods on the properties of plain and blended cement concretes[J].Construction and Building Materials,2010,24(3):308-314.
[12]李 响,阎培渝.高温养护对复合胶凝材料水化程度及微观形貌的影响[J].中南大学学报:自然科学版,2010,41(6):2321-2326.
LI Xiang,YAN Peiyu.Effect of high temperature curing on hydration degree and micro-morphology of complex binders[J].Journal of Central South University:Science and Technology,2010,41(6):2321-2326.
[13]谭克锋,刘 涛.早期高温养护对混凝土抗压强度的影响[J].建筑材料学报,2006,9(4):473-476.
TAN Kefeng,LIU Tao.Effect of high temperature curing on compressive strength of concrete[J].Journal of Building Materials,2006,9(4):473-476.
[14]阎培渝,崔 强.养护制度对高强混凝土强度发展规律的影响[J].硅酸盐学报,2015,43(2):133-137.
YAN Peiyu,CUI Qiang.Effects of curing regimes on strength development of high-strength concrete[J].Journal of the Chinese Ceramic Society,2015,43(2):133-137.
[15]SHI M X,WANG Q,ZHOU Z K.Comparison of the properties between high-volume fly ash concrete and high-volume steel slag concrete under temperature matching curing condition[J].Construction and Building Materials,2015,98:649-655.
[16]水运工程大体积混凝土温度裂缝控制技术规程:JTS 202-1—2010[S].北京:人民交通出版社,2010.
Technical specification for thermal cracking control of mass concrete of port and waterway engineering:JTS 202-1—2010[S].Beijing:China Communications Press,2010.
[17]SUN J W,ZHANG P.Effects of different composite mineral admixtures on the early hydration and long-term properties of cement-based materials:a comparative study[J].Construction and Building Materials,2021,294:123547.
[18]WANG Q,FENG J J,YAN P Y.An explanation for the negative effect of elevated temperature at early ages on the late-age strength of concrete[J].Journal of Materials Science,2011,46(22):7279-7288.
[19]XU G D,TIAN Q,MIAO J X,et al.Early-age hydration and mechanical properties of high volume slag and fly ash concrete at different curing temperatures[J].Construction and Building Materials,2017,149:367-377.
[20]JUNG W,CHOI S J.Effect of high-temperature curing methods on the compressive strength development of concrete containing high volumes of ground granulated blast-furnace slag[J].Advances in Materials Science and Engineering,2017,2017:7210591.
[21]YANG K H,MUN J S,CHO M S.Effect of curing temperature histories on the compressive strength development of high-strength concrete[J].Advances in Materials Science and Engineering,2015,2015:965471.
[22]CUI H Z,LO T Y,ALI MEMON S,et al.Effect of lightweight aggregates on the mechanical properties and brittleness of lightweight aggregate concrete[J].Construction and Building Materials,2012,35:149-158.
[23]LOU B X,MA F H.Crack extension resistance of steam-cured concrete under different curing temperature conditions[J].Theoretical and Applied Fracture Mechanics,2022,119:103331.
[24]江守恒.大体积混凝土实体强度发展规律及其评价方法研究[D].哈尔滨:哈尔滨工业大学,2006.
JIANG Shouheng.Study on the development law and evaluation method of solid strength of mass concrete[D].Harbin:Harbin Institute of Technology,2006.

相似文献/References:

备注/Memo

备注/Memo:

收稿日期:2023-05-05
基金项目:国家重点研发计划项目(2020YFC1909904)
通信作者:李北星(1970-),男,工学博士,教授,博士生导师,E-mail:libx0212@126.com。

常用功能

更新日期/Last Update: 2024-05-20