Title:

Effect of Addition of Shrinkage Reducing Admixture on Properties of Cement Mortar

作者:

任慧韬,郭磊

大连理工大学 建设工程学部,辽宁 大连 116024

Author(s):

REN Hui-tao, GUO Lei

Faculty of Infrastructure Engineering, Dalian University of Technology, Dalian 116024, Liaoning, China

关键词:

减缩剂;  表面张力;  水泥砂浆;  收缩;  抗压强度;  抗折强度

Keywords:

shrinkage reducing admixture;  surface tension;  cement mortar;  shrinkage;  compressive strength;  flexural strength

分类号:

TU528.042

DOI:

-

文献标志码:

A

摘要:

对比研究了减缩剂单掺及与减水剂复掺对砂浆收缩、抗压强度及抗折强度的影响,并采用扫描电子显微镜(SEM)对掺有减缩剂的水泥石水化产物的微观形貌进行了研究。结果表明:减缩剂内掺对砂浆试件有明显的减缩效果,单掺和复掺下的28 d减缩率分别达到了50%和35%,早期减缩效果尤为明显,且早期出现微膨胀现象,膨胀量达到了总收缩的20%,这些膨胀有效补偿了试件的自收缩; 减缩剂的掺入对不同龄期的砂浆抗压强度及抗折强度都有不同程度的不利影响,复掺减缩剂和减水剂可降低这种不利影响,使其控制在10%以内; 掺有减缩剂的水化速度减慢,减缩剂不仅具有降低孔溶液表面张力的物理作用,还具有参与水泥水化反应的化学作用,从而影响水泥的水化产物及浆体的力学性能。

Abstract:

The effect of mixing with shrinkage reducing admixtures(SRA)only and compounding with superplasticizer(SP)on shrinkage, compressive strength and flexural strength of mortar were comparatively investigated. The microstructure of the cement was determined by scanning electron microscopy(SEM), and the effects of SRA on the microstructure of cement hydration production products were studied. Results show that SRA can obviously reduce the shrinkage of mortar. The addition of SRA results in a reduction in shrinkage of 50% and 35%(compounding with SP)at 28 d, as compared to the control mixture. The shrinkage reducing effect of SRA is particularly evident at early age. Mortar containing SRA have indicated an expansion at early age, it's about 20% of total shrinkage, and these expansion effectively compensate the specimen shrinkage. SRA has a certain negative effect on the compressive strength and flexural strength of mortar. Compounding with SRA and SP can reduce the negative effect within 10%. SRA retards hydration of cement pastes and has physical and chemical effects in cement paste. SRA has physical effects to reduce the surface tension of pore solution, also has chemical effects of the hydration of cement to affect cement hydration products and mechanical properties of cement pastes.

参考文献/References:

[1] BYFORS J.Plain Concrete at Early Ages[M].Stockholm:Swedish Cement and Concrete Research Institute,1980.
[2]KASAI Y,YOKOYAMA K,MATSUI L.Tensile Properties of Early-age Concrete[C]//The Society of Materials Science.Proceedings of the 6th International Conference on Mechanical Behaviour of Materials.Tokyo:The Society of Materials Science,1972:163-172.
[3]SHOYA M,SUGITA S,SUGIWARA T.Improvement of Drying Shrinkage and Shrinkage Cracking of Concrete by Special Surfactant[C]//RILEM.Proceedings of the International RILEM Symposium.London:Chapman and Hall,1990:484-495.
[4]BALOGH A.New Admixture Combats Concrete Shrinkage[J].Concrete Construction,1996,41(7):546-551.
[5]NMAI C K,TOMITA R,HONDO F,et al.Shrinkage-reducing Admixtures[J].Concrete International,1998,20(4):31-37.
[6]BENTZ D P,GEIKER M R,HANSEN K K.Shrinkage-reducing Admixtures and Early-age Desiccation in Cement Pastes and Mortars[J].Cement and Concrete Research,2001,31(7):1075-1085.
[7]AI H,YOUNG J F.Mechanisms of Shrinkage Reduction Using a Chemical Admixture[C]//JUSTNES H.Proceedings of the 10th International Congress on the Chemistry of Cement.Gothenburg:Amarkai AB and Congrex,1997:18-22.
[8]FOLLIARD K J,BERKE N S.Properties of High-performance Concrete Containing Shrinkage-reducing Admixture[J].Cement and Concrete Research,1997,27(9):1357-1364.
[9]BERKE N S,DALLAIRE M P,HICKS M C,et al.New Developments in Shrinkage-reducing Admixtures[C]//ACI.Proceedings of the 5th ACI International Conference on Superplasticizers and Other Chemical Admixtures in Concrete.Roma:ACI,1997:971-998.
[10]SHAH S P,KARAGULER M E,SARIGAPHUTI M.Effects of Shrinkage-reducing Admixtures on Restrained Shrinkage Cracking of Concrete[J].ACI Materials Journal,1992,89(3):289-295.
[11]RAJABIPOUR F,SANT G,WEISS J.Interactions Between Shrinkage Reducing Admixtures(SRA)and Cement Paste's Pore Solution[J].Cement and Concrete Research,2008,38(5):606-615.
[12]ZHANG J G,GAO N X,RAN Q P,et al.Effect of Shrinkage Reducing Admixture on Cement Paste Structure Development[J].Journal of Southeast University:Natural Science Edition,2010,40(S2):172-176.
[13]ZHANG Z B,XU L L,CHEN L,et al.Effect of Shrinkage-reducing Admixtures on the Shrinkage and Hydration of Cement-based Materials[C]//ACI.Proceedings of the 9th ACI International Conference on Superplasticizers and Other Chemical Admixtures.Seville:ACI,2009:309-320.
[14]WEISS J,LURA P,RAJABIPOUR F,et al.Performance of Shrinkage-reducing Admixtures at Different Humidity and at Early Ages[J].ACI Materials Journal,2008,105(5):478-486.
[15]SANT G,RAJABIPOUR F,LURA P,et al.Examining Residual Stress Development in Cementitious Materials Experiencing an Early-age Expansion[C]//MALHOTRA V M.Proceedings of the 9th CANMET/ACI International Conference on Recent Advances in Concrete Technology.Warsaw:ACI,2007:1-11.
[16]SANT G,LOTHENBACH B,JUILLAND P,et al.The Origin of Early Age Expansions Induced in Cementitious Materials Containing Shrinkage Reducing Admixtures[J].Cement and Concrete Research,2011,41(3):218-229.
[17]BENTZ D P.Curing with Shrinkage-reducing Admixtures:Beyond Drying Shrinkage Reduction[J].Concrete International,2005,27(10):51-60.
[18]陈美祝,周明凯,吴少鹏,等.减缩剂对水泥基材料早期水化及收缩变形性能的影响[J].武汉大学学报:工学版,2007,40(1):78-82. CHEN Mei-zhu,ZHOU Ming-kai,WU Shao-peng,et al.Effect of Shrinkage-reducing Admixture on Hydration and Shrinkage Deformation of Cement-based Materials at Early Ages[J].Engineering Journal of Wuhan University,2007,40(1):78-82.

相似文献/References:

备注/Memo

备注/Memo:

收稿日期:2012-06-21
基金项目:国家自然科学基金项目(51078058)
作者简介:任慧韬(1973-),男,内蒙古赤峰人,副教授,工学博士,E-mail:renht@dlut.edu.cn。

常用功能

更新日期/Last Update: 2012-09-20