|Table of Contents|

Experimental Research on Post-fire Fracture Failure of Q690D Steel Cross-shaped Welded Joints(PDF)

《建筑科学与工程学报》[ISSN:1673-2049/CN:61-1442/TU]

Issue:
2021年05期
Page:
56-65
Research Field:
Publishing date:

Info

Title:
Experimental Research on Post-fire Fracture Failure of Q690D Steel Cross-shaped Welded Joints
Author(s):
HUANG Xue-wei;  ZHANG Xiao-ge;  WEI Chen-chen;  ZHAO Jun;  GE Jian-zhou
(School of Mechanics and Safety Engineering, Zhengzhou University, Zhengzhou 450001, Henan, China)
Keywords:
Q690D steel;  high temperature;  experimental research;  fracture failure;  welded joint;  ultra low cycle fatigue
PACS:
TU391
DOI:
10.19815/j.jace.2021.01051
Abstract:
In order to study the fracture properties of Q690D high strength steel and welded joints at room temperature and after high temperature, the cross-shaped welded joints representing the actual local welding structure of the beam-to-column joints were selected, and a series of uniaxial tensile tests of Q690D steel and ER80-G weld metal at room temperature and after high temperature were conducted. The elastic modulus, yield strength, ultimate strength and elongation of steel and weld metal after high temperatures were obtained. The cross-shaped welded joints at room temperature and after high temperature were tested under monotonic loading and ultra low cyclic loading. The fracture mechanism of Q690D high strength welded joints was analyzed while the effect of post-fire temperature and loading condition on the fracture behavior of steel and welded joints was discussed. The results show that when the temperature is higher than 600 ℃, the post-fire strength of steel and welded joints decreases and the post-fire deformability increases. The strength of Q690D steel decreases after 800 ℃ high temperature, but the mechanical properties of ER80-G weld metal do not change obviously, causing the result that fracture failure of welded joint does not occur at the weld but at the base metal under monotonic loading after 800 ℃ high temperature. The bearing capacity and deformation capacity of welded joints under cyclic loading are lower than those under monotonic loading. The mechanical properties of steel, weld metal as well as the welded joints obtained from the tests are able to provide basic test data to develop fracture analysis models considering the post-fire effect.

References:

[1] 刘希月,王元清,石永久,等.高强度钢框架梁柱节点焊接构造的断裂性能试验研究[J].工程力学,2018,35(5):54-64.
LIU Xi-yue,WANG Yuan-qing,SHI Yong-jiu,et al.Experimental Study on the Weld Fracture Behavior of High Strength Steel Beam-to-column Connections[J].Engineering Mechanics,2018,35(5):54-64.
[2]施 刚,班慧勇,石永久,等.高强度钢材钢结构研究进展综述[J].工程力学,2013,30(1):1-13.
SHI Gang,BAN Hui-yong,SHI Yong-jiu,et al.Overview of Research Progress for High Strength Steel Structures[J].Engineering Mechanics,2013,30(1):1-13.
[3]KANVINDE A M,DEIERLEIN G G.Cyclic Void Growth Model to Assess Ductile Fracture Initiation in Structural Steels Due to Ultra Low Cycle Fatigue[J].Journal of Engineering Mechanics,2007,133(6):701-712.
[4]BLECK W,DAHL W,NONN A,et al.Numerical and Experimental Analyses of Damage Behaviour of Steel Moment Connection[J].Engineering Fracture Mechanics,2009,76(10):1531-1547.
[5]黄学伟,葛建舟,赵 军,等.Q690D高强钢基于连续损伤模型的断裂破坏预测分析[J].工程力学,2020,37(2):230-240.
HUANG Xue-wei,GE Jian-zhou,ZHAO Jun,et al.Fracture Prediction Analysis of Q690D High Strength Steel Based on Continuum Damage Model[J].Engineering Mechanics,2020,37(2):230-240.
[6]HUANG X W,ZHAO J.A Cumulative Damage Model for Extremely Low Cycle Fatigue Cracking in Steel Structure[J].Structural Engineering and Mechanics,2017,62(2):225-236.
[7]廖芳芳,王 伟,李文超,等.钢结构节点断裂的研究现状[J].建筑科学与工程学报,2016,33(1):67-75.
LIAO Fang-fang,WANG Wei,LI Wen-chao,et al.Review on Research Status of Connection Fracture of Steel Structures[J].Journal of Architecture and Civil Engineering,2016,33(1):67-75.
[8]楼国彪,俞 珊,王 锐.高强度螺栓过火冷却后力学性能试验研究[J].建筑结构学报,2012,33(2):33-40.
LOU Guo-biao,YU Shan,WANG Rui.Mechanical Properties of High-strength Bolts After Fire[J].Journal of Building Structures,2012,33(2):33-40.
[9]AZHARI F,HEIDARPOUR A,ZHAO X L.On the Use of Bernstain-Bezier Functions for Modelling the Post-fire Stress-strain Relationship of Ultra-high Strength Steel(Grade 1 200)[J].Engineering Structures,2018,175:605-616.
[10]刘天姿.高强度Q460钢柱受火后力学性能研究[D].重庆:重庆大学,2015.
LIU Tian-zi.Study on Post-fire Mechanical Behavior of High Strength Q460 Steel Columns[D].Chongqing:Chongqing University,2015.
[11]QIANG X,BIJLAARD F S K,KOLSTEIN H.Post-fire Mechanical Properties of High Strength Structural Steels S460 and S690[J].Engineering Structures,2012,35:1-10.
[12]QIANG X,BIJLAARD F S K,KOLSTEIN H.Post-fire Performance of Very High Strength Steel S960[J].Journal of Constructional Steel Research,2013,80:235-242.
[13]WANG W Y,LIU T Z,LIU J P.Experimental Study on Post-fire Mechanical Properties of High Strength Q460 Steel[J].Journal of Constructional Steel Research,2015,114:100-109.
[14]李国强,吕慧宝,张 超.Q690钢材高温后的力学性能试验研究[J].建筑结构学报,2017,38(5):109-116.
LI Guo-qiang,LÜ Hui-bao,ZHANG Chao.Experimental Research on Post-fire Mechanical Properties of Q690 Steel[J].Journal of Building Structures,2017,38(5):109-116.
[15]ZHANG C T,WANG R H,SONG G B.Post-fire Mechanical Properties of Q460 and Q690 High Strength Steels After Fire-fighting Foam Cooling[J].Thin-walled Structures,2020,156:106983.
[16]HUANG Y H,ONISHI Y,HAYASHI K.Inelastic Behavior of High Strength Steels with Weld Connections Under Cyclic Gradient Stress[C]//WCEE.Proceeding of the 11th World Conference on Earthquake Engineering.Oxford:Elsevier Science Ltd,1996:385-390.
[17]刘希月.基于微观机理的高强钢结构材料与节点的断裂性能研究[D].北京:清华大学,2015.
LIU Xi-yue.Investigations on Fracture Behaviours of High Strength Steel Materials and Connections Based on Micromechanical Models[D].Beijing:Tsinghua University,2015.
[18]GB/T 1591—2018,低合金高强度结构钢[S].
GB/T 1591—2018,High Strength Low Alloy Structural Steels[S].
[19]LIAO F F,WANG M Q,TU L S,et al.Micromechanical Fracture Model Parameter Influencing Factor Study of Structural Steels and Welding Materials[J].Construction and Building Materials,2019,215:898-917.
[20]KANVINDE A M,FELL B V,GOMEZ I R,et al.Predicting Fracture in Structural Fillet Welds Using Traditional and Micromechanical Fracture Models[J].Engineering Structures,2008,30(11):3325-3335.

Memo

Memo:
-
Last Update: 2021-09-01