[1]李富民,杨 俊,施小飞.腐蚀钢绞线预应力混凝土梁的弯曲疲劳性能退化特征[J].建筑科学与工程学报,2016,33(01):22-29.
 LI Fu-min,YANG Jun,SHI Xiao-fei.Degradation Characteristics of Flexural Fatigue Property of Prestressed Concrete Beam with Corroded Steel Strand[J].Journal of Architecture and Civil Engineering,2016,33(01):22-29.
点击复制

腐蚀钢绞线预应力混凝土梁的弯曲疲劳性能退化特征(PDF)
分享到:

《建筑科学与工程学报》[ISSN:1673-2049/CN:61-1442/TU]

卷:
33卷
期数:
2016年01期
页码:
22-29
栏目:
出版日期:
2016-01-29

文章信息/Info

Title:
Degradation Characteristics of Flexural Fatigue Property of Prestressed Concrete Beam with Corroded Steel Strand
作者:
李富民杨 俊施小飞
中国矿业大学江苏省土木工程环境灾变与结构可靠性重点实验室
Author(s):
LI Fu-min YANG Jun SHI Xiao-fei
Jiangsu Key Laboratory of Environmental Impact and Structural Safety in Engineering, China University of Mining and Technology
关键词:
预应力混凝土梁钢绞线耐久性氯盐环境腐蚀疲劳弯曲刚度
Keywords:
prestressed concrete beam steel strand durability chloride environment corrosion fatigue flexural rigidit
分类号:
-
DOI:
-
文献标志码:
A
摘要:
采用与实际氯盐环境腐蚀效果更为接近的内掺盐加速腐蚀方式,制作4根不同掺盐率的钢绞线预应力混凝土梁试件并放置90 d以产生不同程度的腐蚀,然后对腐蚀梁试件进行疲劳加载直至出现断丝破坏,其中在每1×105 次疲劳作用后进行1次静力加载试验,以考察疲劳破坏、疲劳寿命退化以及弯曲刚度退化等特征。结果表明:钢绞线表现出典型的坑蚀特征;坑蚀钢丝在疲劳作用下会出现多个疲劳裂纹,其中1个裂纹最终发展至瞬断而成为梁疲劳破坏的标志;钢丝疲劳断口呈现出典型的宏观脆性断口特征,断口表面清晰可见蚀坑区、疲劳断裂区及瞬断区;梁的疲劳寿命随掺盐率增加呈指数函数关系退化;疲劳作用导致腐蚀梁的荷载挠度曲线由前、后2个刚度不同但都近似呈直线的区段组成;氯盐作用和疲劳作用愈强,二者叠加引起梁的刚度退化也愈显著。
Abstract:
The accelerated corrosion method of mixing salt into concrete which had a similar corrosion result with the situation of actual chloride environment was used. Four prestressed concrete beams with steel strands and different salt contents were fabricated and placed for 90 d to achieve different corrosion degrees. Then the corroded specimens were loaded in fatigue until to failure with one steel wire fracturing, and a static loading test was executed after every 1×105 times fatigue loading. Based on the experiment, the characteristics of fatigue failure, fatigue life degradation and flexural rigidity degradation were studied. The results show that the steel strands are corroded in typical pitting appearance. Multiple fatigue cracks appear on the pitting corroded wires under the action of fatigue, and one of them develops to fracture ultimately and marks the failure state. The fatigue fractures of wires show typical macrobrittle characteristic. The pitting corrosion region, fatigue fracture region and final fracture region are presented clearly in the fatigue fractures. The fatigue life degenerates in the exponential function law with the increase of salt content. For the influence of fatigue action, the loaddeflection curve of corroded beam is changed to be composed with two approximate straight lines with different slopes. The stronger the chloride action and fatigue action are, the more prominent the rigidity of the beam degenerates.

参考文献/References:

相似文献/References:

[1]王作虎,詹界东,杜修力.无粘结预应力CFRP筋混凝土梁抗弯试验[J].建筑科学与工程学报,2014,31(02):84.
 [J].Journal of Architecture and Civil Engineering,2014,31(01):84.
[2]方 梅,李 漫,李 杉.钢管混凝土柱-预应力混凝土梁节点抗震性能试验[J].建筑科学与工程学报,2016,33(03):110.
 FANG Mei,LI Man,LI Shan.Experiment on Seismic Performance of Connection BetweenConcrete-filled Steel Tubular Column and Prestressed Concrete Beam[J].Journal of Architecture and Civil Engineering,2016,33(01):110.
[3]王 钧,李 婷,任靖豪.大直径高强钢绞线预应力混凝土梁受力性能[J].建筑科学与工程学报,2017,34(02):103.
 WANG Jun,LI Ting,REN Jing-hao.Mechanical Performances of Prestressed Concrete Beams with Large-diameter High-strength Steel Strands[J].Journal of Architecture and Civil Engineering,2017,34(01):103.
[4]杨 鸥,张晓非,霍静思,等.预应力混凝土梁疲劳性能研究现状[J].建筑科学与工程学报,2017,34(04):85.
 YANG Ou,ZHANG Xiao-fei,HUO Jing-si,et al.Research Status of Fatigue Performance of Prestressed Concrete Beam[J].Journal of Architecture and Civil Engineering,2017,34(01):85.
[5]羊日华,刘 欢,张旭辉,等.腐蚀预应力混凝土梁抗剪性能试验[J].建筑科学与工程学报,2018,35(05):134.