[1]谢建和,冯 源,薛紫欣,等.碳化和加热改性石材微粉对水泥浆体性能影响试验[J].建筑科学与工程学报,2022,39(02):87-96.[doi:10.19815/j.jace.2021.03043]
 XIE Jian-he,FENG Yuan,XUE Zi-xin,et al.Experiment on Effects of Carbonization and Heating Modification of Stone Micro Powder on Performance of Cement Paste[J].Journal of Architecture and Civil Engineering,2022,39(02):87-96.[doi:10.19815/j.jace.2021.03043]
点击复制

碳化和加热改性石材微粉对水泥浆体性能影响试验(PDF)
分享到:

《建筑科学与工程学报》[ISSN:1673-2049/CN:61-1442/TU]

卷:
39卷
期数:
2022年02期
页码:
87-96
栏目:
结构工程
出版日期:
2022-03-30

文章信息/Info

Title:
Experiment on Effects of Carbonization and Heating Modification of Stone Micro Powder on Performance of Cement Paste
文章编号:
1673-2049(2022)02-0087-10
作者:
谢建和12冯 源2薛紫欣2李丽明2麦子桦2张佰发2
(1. 广州理工学院 建筑工程学院,广东 广州 510540; 2. 广东工业大学 土木与交通工程学院,广东 广州 510006)
Author(s):
XIE Jian-he12 FENG Yuan2 XUE Zi-xin2 LI Li-ming2 MAI Zi-hua2 ZHANG Bai-fa2
(1. School of Civil Engineering and Architecture, Guangzhou Institute of Science and Technology, Guangzhou 510540, Guangdong, China; 2. School of Civil and Transportation Engineering, Guangdong University of Technology, Guangzhou 510006, Guangdong, China)
关键词:
石材微粉 碳化 加热 改性 水泥浆体
Keywords:
stone micro powder carbonization heating modification cement paste
分类号:
TU973.2
DOI:
10.19815/j.jace.2021.03043
文献标志码:
A
摘要:
为提高石材制品生产过程中产生的废弃微粉的再生利用率,通过CO2碳化和加热预处理,探讨花岗岩石材微粉替代水泥制备水泥基浆体的改性方法。以石材微粉替代率(0%、10%、20%、30%)、石材微粉粒径(2组)、碳化时长(0、24 h)、加热温度(室温、400 ℃、600 ℃)为试验变量,并考虑7 d和28 d龄期的影响,开展了改性再生微粉水泥基浆体流动性和抗压性能的试验研究,分析了各变量对其流动性、抗压强度和破坏模式的影响规律。在此基础上,结合X射线衍射(XRD)测试,揭示石材微粉的改性机理。结果表明:石材微粉的掺入会造成水泥浆体强度的明显下降; 加热改性在一定程度上可以减少石材微粉对水泥浆体的负面作用,其中400 ℃加热改性的效果最佳; 碳化改性该类石材微粉对水泥基浆体的增强效果不佳; 改性前后的石材微粉掺入均不会对水泥浆体的流动性产生明显影响。
Abstract:
In order to improve the recycling rate of waste micro powder produced in the production of stone products, through CO2 carbonization and heating pretreatment, the modification methods of using the granite micro powder instead of cement to prepare cement-based paste were studied. Taking stone powder content(0%, 10%, 20%, 30%), stone powder particle size(2 groups), carbonization time(0, 24 h), heating temperature(room temperature, 400 ℃, 600 ℃)as the experimental variables, as well as considering the influence of the curing age of 7 d and 28 d,the experimental study on the fluidity and compressive properties of modified recycled micro powder cement-based pastes was carried out, and the effect laws of various variables on the fluidity, compressive strength and failure mode were analyzed. On the basis, the modification mechanism of stone powder was revealed by X-ray diffraction(XRD)test. The results show that the compressive strength of cement paste decreases obviously with the incorporation of stone micro powder, while the heat modification can reduce the negative effect of stone micro powder on the cement paste to a certain extent, and the optimal heat temperature is 400 ℃. Carbonization modification of stone micro powder has no obvious enhancement effect on the compressive of cement paste. The fluidity of cement paste will not be affected by the incorporation of stone powder before and after modification.

参考文献/References:

[1] ZULCAO R,CALMON J L,REBELLO T A,et al.Life Cycle Assessment of the Ornamental Stone Processing Waste Use in Cement-based Building Materials[J].Construction and Building Materials,2020,257:119523.
[2]YURDAKUL M.Natural Stone Waste Generation from the Perspective of Natural Stone Processing Plants:An Industrial-scale Case Study in the Province of Bilecik,Turkey[J].Journal of Cleaner Production,2020,276:123339.
[3]VIJAYALAKSHMI M,SEKAR A S S,PRABHU G G.Strength and Durability Properties of Concrete Made with Granite Industry Waste[J].Construction and Building Materials,2013,46:1-7.
[4]YANG R,YU R,SHUI Z,et al.Environmental and Economical Friendly Ultra-high Performance-concrete Incorporating Appropriate Quarry-stone Powders[J].Journal of Cleaner Production,2020,260:121112.
[5]MARQUES F C,SILVA J C M,LIBARDI C P,et al.Hydrogen Production by Photovoltaic-electrolysis Using Aqueous Waste from Ornamental Stones Industries[J].Renewable Energy,2020,152:1266-1273.
[6]LI H J,HUANG F L,CHENG G Z,et al.Effect of Granite Dust on Mechanical and Some Durability Properties of Manufactured Sand Concrete[J].Construction and Building Materials,2016,109:41-46.
[7]CHAJEC A.Towards the Sustainable Use of Granite Powder Waste for Manufacturing of Cementitious Composites[J].MATEC Web of Conferences,2020,322:01005.
[8]肖 杰,屈文俊,朱 鹏.不同粗细骨料组合下的混凝土耐硫酸腐蚀研究[J].建筑科学与工程学报,2016,33(6):81-87.
XIAO Jie,QU Wen-jun,ZHU Peng.Research on Concrete Sulfuric Acid Resistance with Different Types of Coarse and Fine Aggregates[J].Journal of Architecture and Civil Engineering,2016,33(6):81-87.
[9]刘数华,阎培渝.石灰石粉对水泥浆体填充效应和砂浆孔结构的影响[J].硅酸盐学报,2008,36(1):69-72,77.
LIU Shu-hua,YAN Pei-yu.Influence of Limestone Powder on Filling Effect of Cement Paste and Pore Structure of Sand Grout[J].Journal of the Chinese Ceramic Society,2008,36(1):69-72,77.
[10]SAVADKOOHI M S,REISI M.Environmental Protection Based Sustainable Development by Utilization of Granite Waste in Reactive Powder Concrete[J].Journal of Cleaner Production,2020,266:121973.
[11]JAIN K L,SANCHETI G,GUPTA L K.Durability Performance of Waste Granite and Glass Powder Added Concrete[J].Construction and Building Materials,2020,252:119075.
[12]任卫岗,庄一舟,于丽雪.花岗岩石粉-高韧性水泥基复合材料的制备与性能[J].科学技术与工程,2016,16(17):269-274.
REN Wei-gang,ZHUANG Yi-zhou,YU Li-xue.Preparation and Properties of Granite Stone Powder-high Toughness Cementitious Composite[J].Science Technology and Engineering,2016,16(17):269-274.
[13]HEBHOUB H,AOUN H,BELACHIA M,et al.Use of Waste Marble Aggregates in Concrete[J].Construction and Building Materials,2010,25(3):1167-1171.
[14]BINICI H,SHAH T,AKSOGAN O,et al.Durability of Concrete Made with Granite and Marble as Recycle Aggregates[J].Journal of Materials Processing Technology,2008,208(1/2/3):299-308.
[15]李相国,李孟蕾,马保国,等.改性花岗岩石粉对水泥的性能影响[J].混凝土,2013(8):87-90.
LI Xiang-guo,LI Meng-lei,MA Bao-guo,et al.Impact on the Performance of the Modified Granite Stone Powder for Cement[J].Concrete,2013(8):87-90.
[16]XUAN D,ZHAN B,POON C S.Assessment of Mechanical Properties of Concrete Incorporating Carbonated Recycled Concrete Aggregates[J].Cement and Concrete Composites,2016,65:67-74.
[17]应敬伟,蒙秋江,肖建庄.再生骨料CO2强化及其对混凝土抗压强度的影响[J].建筑材料学报,2017,20(2):277-282.
YING Jing-wei,MENG Qiu-jiang,XIAO Jian-zhuang.Effect of CO2-modified Recycled Aggregate on Compressive Strength of Concrete[J].Journal of Building Materials,2017,20(2):277-282.
[18]ZHANG J K,SHI C J,LI Y K,et al.Influence of Carbonated Recycled Concrete Aggregate on Properties of Cement Mortar[J].Construction and Building Materials,2015,98:1-7.
[19]WANG J J,MU M L,LIU Y L.Recycled Cement[J].Construction and Building Materials,2018,190:1124-1132.
[20]WONG Y D,SUN D D,LAI D.Value-added Utilisation of Recycled Concrete in Hot-mix Asphalt[J].Waste Management,2007,27(2):294-301.
[21]KELESTEMUR O,ARICI E,YILDIZ S,et al.Performance Evaluation of Cement Mortars Containing Marble Dust and Glass Fiber Exposed to High Temperature by Using Taguchi Method[J].Construction and Building Materials,2014,60:17-24.
[22]水泥胶砂流动度测定方法:GB/T 2419—2005[S].北京:中国标准出版社,2005.
Text Method for Fluidity of Cement Mortar:GB/T 2419—2005[S].Beijing:Standards Press of China,2005.
[23]建筑砂浆基本性能试验方法标准:JGJ/T 70—2009[S].北京:中国建筑工业出版社,2009.
Standard for Text Method of Performance on Building Mortar:JGJ/T 70—2009[S].Beijing:China Architecture & Building Press,2009.
[24]DA SILVA J L,DA CUNHA CAMPOS D B,LORDSLEEM A C,et al.Influence of the Partial Substitution of Fine Aggregate by Granite Powder in Mortar on the Process of Natural Carbonation[J].Waste Management & Research,2020,38(3):254-262.
[25]ZHANG B F,GUO H Z,YUAN P,et al.Geopolymerization of Halloysite via Alkali-activation:Dependence of Microstructures on Precalcination[J].Applied Clay Science,2020,185:105375.
[26]英丕杰,刘福胜,孙 雷,等.花岗岩石粉水工混凝土工作性能试验研究[J].人民黄河,2014,36(2):126-128.
YING Pi-jie,LIU Fu-sheng,SUN Lei,et al.Study on Working Performance of Hydraulic Concrete Mixed with Granite Powder[J].Yellow River,2014,36(2):126-128.
[27]GENCEL O,KOKSAL F,OZEL C,et al.Combined Effects of Fly Ash and Waste Ferrochromium on Properties of Concrete[J].Construction and Building Materials,2012,29:633-640.
[28]GENCEL O,OZEL C,KOKSAL F,et al.Properties of Concrete Paving Blocks Made with Waste Marble[J].Journal of Cleaner Production,2012,21(1):62-70.
[29]SETHY K P,PASLA D,CHANDRA SAHOO U.Utilization of High Volume of Industrial Slag in Self Compacting Concrete[J].Journal of Cleaner Production,2016,112:581-587.
[30]MITHUN B M,NARASIMHAN M C.Performance of Alkali Activated Slag Concrete Mixes Incorporating Copper Slag as Fine Aggregate[J].Journal of Cleaner Production,2016,112:837-844.
[31]SADEK D M,EL-ATTAR M M,ALI H A.Reusing of Marble and Granite Powders in Self-compacting Concrete for Sustainable Development[J].Journal of Cleaner Production,2016,121:19-32.
[32]ZHANG K Q,LIU F S,YUE Q,et al.Effect of Granite Powder on Properties of Concrete[J].Asia-Pacific Journal of Chemical Engineering,2020,15(S1):e2468.
[33]GAO X,YUAN B,YU Q L,et al.Characterization and Application of Municipal Solid Waste Incineration(MSWI)Bottom Ash and Waste Granite Powder in Alkali Activated Slag[J].Journal of Cleaner Production,2017,164:410-419.
[34]VARDHAN K,GOYAL S,SIDDIQUE R,et al.Mechanical Properties and Microstructural Analysis of Cement Mortar incorporating Marble Powder as Partial Replacement of Cement[J].Construction and Building Materials,2015,96:615-621.
[35]ABD ELMOATY A E M.Mechanical Properties and Corrosion Resistance of Concrete Modified with Granite Dust[J].Construction and Building Materials,2013,47:743-752.

相似文献/References:

[1]郭猛,刘洪,白文静.混凝土桥梁结构的等耐久性设计[J].建筑科学与工程学报,2010,27(01):117.
 GUO Meng,LIU Hong,BAI Wen-jing.Equal Durability Design of Concrete Bridge Structure[J].Journal of Architecture and Civil Engineering,2010,27(02):117.
[2]应敬伟,肖建庄.再生骨料取代率对再生混凝土耐久性的影响[J].建筑科学与工程学报,2012,29(01):56.
 YING Jing-wei,XIAO Jian-zhuang.Influence of Recycled Aggregate Replacement Ratio on Durability of Recycled Aggregate Concrete[J].Journal of Architecture and Civil Engineering,2012,29(02):56.
[3]张 佶,屈文俊,朱 鹏.迁移型阻锈剂对混凝土中钢筋的长期影响[J].建筑科学与工程学报,2020,37(06):117.
 ZHANG Ji,QU Wen-jun,ZHU Peng.Long-term Effects of Migrating Corrosion Inhibitors on Steel Bars in Concrete[J].Journal of Architecture and Civil Engineering,2020,37(02):117.

备注/Memo

备注/Memo:
收稿日期:2021-03-09
基金项目:国家自然科学基金项目(12072078,12032009); 广东省自然科学基金项目(2019B151502004); 广东省青年优秀科研人才国际培养计划项目(2022)
作者简介:谢建和(1980-),男,广东阳江人,教授,博士研究生导师,工学博士,E-mail:jhxie@gdut.edu.cn。
更新日期/Last Update: 2022-03-20